Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 367 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP EL002 PEI
LNP* Lubricomp* EL002 is a compound based on Polyetherimide resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ISO 75/Af
Solvay TECHNYLSTARâ„¢ S 218 MZ20 V10 Black 2N PA6, 20% mineral, 10% glass filled, DRY
Description: TECHNYL STAR Polyamide, 20% mineral filled and 10% of glass fiber reinforced, heat stabilized, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe a..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C

@Thickness 6.40 mm
367 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE
High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C

@Thickness 6.40 mm
367 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific)
High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C

@Thickness 6.40 mm
367 °F

@Thickness 0.252 in
unannealed; ASTM D 648
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Europe-Africa-Middle East)
High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Valox® IQ507 PBT+PC
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Valox® IQ507 PBT+PC (Asia Pacific)
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics Valox® IQ507 PBT+PC (Europe-Africa-Middle East)
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C

@Thickness 3.20 mm
367 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66
LNP* STAT-LOY* 9X03508 is a compound based on PPO+PA66 resin containing Proprietary Filler(s). Added features of this material include: Antistatic, Flame Retardant, High Impact.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C

@Thickness 3.20 mm
367 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-LOY 9X03508 PPO+PA66 (Asia Pacific)
LNP* Stat-loy* 9X03508 is a compound based on PPO+PA66 resin containing Flame Retardant, Anti-Static. Added features of this material include: Antistat, Flame Retardant, High Impact.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT
LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP WH0270B PBT (Asia Pacific)
LNP THERMOCOMP* WH0270B is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
80*10*4 s=60mm; ISO 75-1 a
Sax Polymers SAXAMID 136F6Q32 Nylon 6, 30% Glass Fiber
SAXAMID 136F6Q32 is a high-impact-modified polyamide 6 injection-molding-grade reinforced with 30% glass fibers . Beside the high impact strength at low temperatures this grade shows very good proce..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
Plenco 00732 Melamine-Phenolic, Granular, Transfer Molded
PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
Plenco 00755 Melamine-Phenolic, Granular, Transfer Molded
PLENCO 00755 is a melamine-phenolic copolymer molding compound offering excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 00755..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
Plenco 5482 Phenolic, Granular, Transfer Molded
PLENCO 05482 is an organic reinforced phenolic molding compound formulated with graphite to improve the abrasion resistance. 05482 is available in black and brown. 05482 is not recommended for elect..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
Plenco 7507 Phenolic, Granular, Injection Molded
PLENCO 07507 is an organic reinforced phenolic molding compound offering improved dimensional stability under humid conditions. 07507 offers excellent resistance to degradation from detergent solut..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
Plenco 4311 Phenolic, Granular, Compression Molded
PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized..
Deflection Temperature at 1.8 MPa (264 psi) 186 °C
367 °F
ASTM D648
A. Schulman ComAlloy Hiloy® 431 Glass Reinforced, PBT Alloy
Data provided by the manufacturer, ComAlloy International Company.15% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.