Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 180 - 200 °C | 356 - 392 °F | Injection; ISO 75-A |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 180 - 200 °C | 356 - 392 °F | Injection; ISO 75-A |
Raschig Group AMPLA® 7250 melamine-modified polyester Cellulose reinforced melamine-modified Polyester molding compound. Very good electrical values, excellent heat resistance, excellent surface quality, low post shrinkage. This product meets the allow.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 180 - 200 °C | 356 - 392 °F | Injection; ISO 75-A |
Raschig Group AMPLA® 7500 melamine-modified polyester Organically and inorganically filled melamine modified Polyester molding compound. Low post-shrinkage, very good electrical values, excellent heat resistance, very good sliding behavior and wear sta.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 200 °C | 158 - 392 °F | Average value: 134 °C Grade Count:11 |
Overview of materials for PET + PBT Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PET + PBT Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 70.0 - 200 °C | 158 - 392 °F | Average value: 129 °C Grade Count:20 |
Overview of materials for Nylon 6, 20% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 56.0 - 200 °C | 133 - 392 °F | Average value: 108 °C Grade Count:10 |
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 180 - 200 °C | 356 - 392 °F | ISO 75 Af |
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by .. |