- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 415 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 415 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Annealed; ASTM D648 |
| Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK)
(Unverified Data**) AvaSpire AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Solvay Specialty Polymers KetaSpire® KT-820 GF13 Polyetheretherketone (PEEK)
(Unverified Data**) KetaSpire KT-820 is a low flow, 13% glass fiber reinforced grade of polyetheretherketone (PEEK). The glass fiber content is optimized to provide a balance of strength and stiffness with toughness-re.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Annealed, 0.125 in bars; ASTM D648 |
| PolyOne Edgetek® RA-20CF/000 Polyarylsulfone, Carbon Fiber Reinforced
(discontinued **) Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6 GF40 IM2 NAT 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedUL File Number: E157318Processing Meth.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP WFP36 PBT LNP LUBRICOMP* WFP36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON AE004 ABS LNP STAT-KON* AE004 is a compound based on ABS resin containing 20% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP EC002XXQ PEI LNP* THERMOCOMP* EC002XXQ is a compound based on Polyetherimide containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP QC006I PA 6/10 LNP THERMOCOMPâ„¢ QC006I is a compound based on Nylon 6/10 containing 30% Carbon Fiber. Added features of this grade include: High Impact. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP RX07034 PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RX07034 is a compound based on PA 66 resin containing Glass Fiber. Added features include; Low Smoke, Easy Molding, Cross Linkable under Beta-or Gamma Radiation; Specially developed.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP QF00A PA6.10 LNP* THERMOCOMP* QF00A is a compound based on Nylon 6/10 containing 50% Glass Fiber. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP Verton PV00A PA 6 (Europe-Africa-Middle East) LNP* Verton* PV00A is a compound based on Nylon 6 resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af |
| Vyncolit X7012 Glass Fiber Reinforced Novolac Phenolic Novolac resin based, glass fiber and glass beads reinforced. High mechanical strength even at high temperatures in Long Life CoolantsInformation provided by Sumitomo Bak North America, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 213 °C | >= 415 °F | ISO 75 Af |
| Vyncolit A2710 Glass Fiber Reinforced Novolac Phenolic Vyncolit A2710 is a glass fiber reinforced phenolic molding compound with excellent mechanical and thermal properties.Information provided by Sumitomo Bak North America, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | dry; ISO 75-1/-2 |
| DSM Novamid® 1010GN2-30 NAT/BK37 PA6-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Asahi Kasei Thermylon® NSG-440A 60% Ceramic and Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||