Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 426 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
ASTM D648
Oxford Polymers Oxnilon 66-ST-14GF 14% Glass Fiber Reinforced, Impact Modified Nylon 66 for Injection Molding
14% Glass Fiber Reinforced, Impact Modified Nylon 66 for Injection MoldingInformation provided by Oxford Polymers.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
ASTM D648
Plenco 51240 PET, Pellet, Injection Molded, Blue  (discontinued **)
PLENCO 51240 is an engineering grade glass reinforced flame retarded recycled polyethylene terephthalate resin designed for excellent dimensional stability. It is UL listed.Information supplied by P..
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Europe-Africa-Middle East)
LNP* Lubricomp* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Unannealed; ASTM D648
Techmer ES Elastoblend® PA6/6 GF14 IM4 HS L BKN 14% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri..
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Unannealed; ASTM D648
Techmer ES HiFill® PA6/6 GF33 BK 33% Glass Filled (Dry)
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and Heat StabilizedAppearanc..
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI
LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP EC006 PEI (Asia Pacific)
LNP THERMOCOMP* EC006 is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP JF004ER PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF-1004 S-3 is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP JF004LZ PES
LNP* Thermocomp* JF004LZ is a compound based on PES containing 20% Glass Fiber. Added features include: Extrusion Grade, Low Extractible.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP JF004RXP PES (Europe-Africa-Middle East)
LNP* Thermocomp* JF004RXP is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Mold Release.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66
LNP* THERMOCOMP* RF0029S is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific)
LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF0039S PA 66
LNP THERMOCOMP* RF0039S is a compound based on Nylon 66 resin containing 15% Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C

@Thickness 3.20 mm
426 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RX06420 PA 66
LNP* Thermocomp* RX06420 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding, Low Extractible, Mold Release.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66
LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
ISO 75-1, 2
Polyplastics FR-PET® BLR6001MZ Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET)
Information provided by PolyPlastics.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
DIN 53461
Polyram PlusTek PA830 Nylon 6.6, Impact Modified
Impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
DIN 53461
Polyram PlusTek PA860 Nylon 6.6, Impact Modified
Super tough - impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
0.125";; ASTM D648
Diamond Polymers NYLON 6001GF33 33% Glass Filled Polyamide
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C

@Thickness 3.20 mm
426 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP VERTON PX91060 PA 6
LNP* VERTON* PX91060 is a compound based on Nylon 6 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
Deflection Temperature at 1.8 MPa (264 psi) 219 °C

@Thickness 3.20 mm
426 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP VERTON PX91060 PA 6 (Asia Pacific)
LNP* Verton* PX91060 is a compound based on Nylon 6 resin containing Long Glass Fiber.