Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 468 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 242 °C

@Thickness 3.18 mm
468 °F

@Thickness 0.125 in
Annealed; ASTM D648
PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66)
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Plastcom SLOVAMID 66 GF 15 GB 25 TS PA66, 15% glass fibre, 25% glass beads
FeaturesPA 66 chemically reinforced with 15 % glass fibre and with the content of 25% glass beads, thermo stable. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical p..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C

@Thickness 3.20 mm
468 °F

@Thickness 0.126 in
Unannealed; ASTM D648
Ovation Polymers Opnyl LSE - OP66GF3015 Nylon 66
Low surface energy Nylon 66 for demanding applications such as bearings, bushes, rods and gearsAll properties after 48hrs conditioning at 23°C/50% RH
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ASTM D648
Oxford Polymers Oxnilon 66-13GF 13% Glass Fiber Filled Nylon 66 for Injection Molding
13% Glass Fiber Filled Nylon 66 for Injection MoldingInformation provided by Oxford Polymers.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75, ASTM D648
Nilit Nilamid A G5 FR PH2 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
Description: Nilamid A G5 FR PH2 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optim..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75, ASTM D648
Nilit Nilamid A G5 FR C4 25% Glass Fiber Reinforced, Flame Retardant PA66 (with Halogens)
Description: Nilamid A G5 FR C4 combines excellent mechanical performance with flame retardancy. The halogenated flame retardant system used in this product allows a wide range of colors. This produ..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Lehmann & Voss LUVOCOM® 8-7190 High impact polyamide, with carbon fiber, toughness-modified
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Especially suitable at dynamic..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66
LNP* LUBRICOMP* RFG16S is a compound based on Nylon 66 resin containing 5% Graphite, 30% Glass Fiber. Added features of this material include: Heat Stabilized, Wear Resistant.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66
LNP* LUBRICOMP* RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66
LNP* STAT-KON* REL42 is a compound based on Nylon 66 resin containing 20% PTFE, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON REL42 PA 66 (Asia Pacific)
LNP* Stat-kon* REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66
LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C

@Thickness 3.20 mm
468 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON RX05488 PA 66
LNP STAT-KON* RX05488 is a compound based on Nylon 66 resin containing Carbon Fiber, Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Electrically Conductive.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP RF006SXZ PA 66
LNP* THERMOCOMP* RF006SXZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added feature of this material is: Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C

@Thickness 3.20 mm
468 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP THERMOCOMP RX05491 PA 66
LNP* Thermocomp* RX05491 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
80*10*4 s=60mm; ISO 75-1 a
Sax Polymers SAXAMID 226F5RY01 Nylon 6.6, 25% Glass Fiber
SAXAMID 226F5RY01 is a polyamide 6.6 injection-molding-grade reinforced with 25% glass fibers. It has a halogen-free flame retardant and UL listed.Information provided by SAX Polymers
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66
LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C

@Thickness 3.20 mm
468 °F

@Thickness 0.126 in
unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON RE0069S PA 66
LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75-1, 2
Polyplastics FR-PET® B3045FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
Information provided by PolyPlastics.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75-1/-2
DuPont Performance Polymers Rynite® FG530 NC011 Polyethylene Terephthalate (PET)  (Unverified Data**)
30% Glass Reinforced Polyethylene Terephthalate Developed for Food Contact ApplicationsRynite FG530 NC011is a 30% glass fiber reinforced modified polyethylene terephthalate resin. It has been develo..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® 79G13HSL NC010 Nylon 66  (Unverified Data**)
13% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 79G13HSL is a 13% glass fiber reinforced heat stabilized lubricated slightly toughened polyamide 66 for injection molding. It has im..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Eurostar Staramide AG3X3 PA66, Glass Fiber Reinforced, Impact Modified, Injection Molding
Staramide AG3X3 is an Impact Modified, Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75
BASF Ultramid® N-276 BK ND 3007 40% Glass/Mineral Filled PA66
Description: Ultramid N-276 BK ND3007 is a 40% mineral/glass reinforced, heat stabilized injection molding PA6/6.Information provided by BASF
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75
BASF Ultramid® N-276 NF3001 40% Glass/Mineral Filled PA66 (Dry)
Ultramid N-276 NF3001 is a 40% mineral/glass reinforced, heat stabilized injection molding nylon 6/6.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ASTM D648
Asia International Enterprise (Hong Kong) 60G2-13GF Nylon 66, 13% Filled
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® 79G13HSL NC010 Nylon 66  (Unverified Data**)
Zytel® 79G13HSL is a 13% glass fiber reinforced, heat stabilized, lubricated slightly toughened polyamide 66 for injection molding. It has improved impact resistance.Information provided by DuPont ..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
DAM; ISO 75-1/-2
DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66  (Unverified Data**)
25% Glass Reinforced Flame Retardant Polyamide 66 Zytel FR50 BK505 is a 25% glass fiber reinforced flame retardant black polyamide 66 resin for injection molding.Information provided by DuPont Perfo..
Deflection Temperature at 1.8 MPa (264 psi) 242 °C
468 °F
ISO 75-1/-2
DuPont Performance Polymers Rynite® FG530 NC011 PET  (Unverified Data**)
Rynite® FG530 NC011is a 30% glass fiber reinforced modified polyethylene terephthalate resin. It has been developed for consideration into applications for the food industry.Information provided by..