Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 527 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
STN EN ISO 75-2 (A)
Plastcom SLOVAMID® 6/6T GF 35 TS PA6/6T reinforced with glass fiber, improved heat resistance
PA 6/6T for injection molding, reinforced with 35% of glass fiber, for moldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry, improved..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ASTM D648
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a
AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese VECTRA E135i LCP, 35% Glass Reinforced  (Unverified Data**)
35% glass fiber filled /Higher weldline strength.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese VECTRA S540 LCP, 40% Mineral Reinforced  (Unverified Data**)
40% mineral filled grade, low warpage high flow.40% mineral filled grade, low warpage high flow.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese ZENITE 5115L LCP, 15% Glass Reinforced  (Unverified Data**)
Zenite® 5115L is a 15% glass fiber reinforced liquid crystal polymer for injection molding with improved toughness.15% glass-reinforced, lubricatedInformation provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese ZENITE 5130L LCP, 30% Glass Reinforced  (Unverified Data**)
Zenite 5130L is a 30% glass-reinforced LCP resin with improved toughness30% glass-reinforced, lubricatedInformation provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Lehmann & Voss LUVOCOM® 20-0659 Polyphthalamide, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Lehmann & Voss LUVOCOM® 204-8468 Polyphthalamide, with carbon fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Lehmann & Voss LUVOCOM® 20-7094 Polyphthalamide, with carbon fiber and PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Low influence from moisture an..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Lehmann & Voss LUVOCOM® 1105/GF/14 PEEK, with glass fiber
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Dynamic stressed parts.Chemical and hydrolysis resistance parts, non f..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
LATI Latilub 57-30GRTS G/20 PPA, 20% Glass Fiber Reinforced
Self-lubricating product based on Semi-aromatic polyamide (PPA). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Shinil Chemical SHINCON PPS Electro Conductive Polymer
SHINCON is the product line of SHINIL's electrically conductive compound which is able to dissipate the electrostatic charge (ESD) effectively. Shinil has developed SHINCON products using Shinil's ..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Shinil Chemical SHINCON PPS-CNT LCD Rack
LCD Rack is used to transfer or bake LCD frame in the electronic assembly or LCD packaging assembly line. Current LCD Rack is made of poly ether ether ketone (PEEK) with carbon fiber (CF). Since b..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Post Baked; ASTM D648A
Sumitomo Bakelite North America E 8354A-2 Short Glass Fiber Reinforced Epoxy
E 8354A-2 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by Sumito..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP UF003AS PPA (Europe-Africa-Middle East)
LNP* THERMOCOMP* UF003AS is a compound based on Polyphthlamide resin containing Glass Fiber. Added features include; Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON UX03320 PPA (Europe-Africa-Middle East)
VERTON* UX03320 is a compound based on Polyphthalamide resin containing Long Glass.
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1/-2
DSM Stanyl® TW200FM33 Nylon 46-30% Glass and Mineral Reinforced (European Grade) (Dry)
Stanyl is a high performance polyamide providing good performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temper..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1/-2
DSM Stanyl® TW241F3 Nylon 46-15% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Dry)
Stanyl is a high performance polyamide providing performance and value across a broad range of automotive and electronic applications. Stanyl offers:Highest mechanical properties at high temperature..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4164 black 9225 PA*-GF30
Product description: Grivory XE 4164 black 9225 is a 30% glass fiber reinforced engineering thermoplastic material based on a semicrystalline, partially aromatic copolyamide. ISO polymer designation..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO-R 75 Method A
Hippe PAI Polyamide-imide
Particularly used where high strength in a wide range of temperature (-190°C…+260°C), high notched strength and very good dielectric properties are required. Features good chemical stability, fl..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
HDT/A; ISO 75-1/2
Akro-Plastic Akromid® T1 GF 30 9 (3498) PPA Dry, 30% Glass Filled
The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese VECTRA E135i LCP, 35% Glass Reinforced
35% glass fiber filled /Higher weldline strength.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ASTM D 648
Celanese Zenite® 5145L WT010 LCP
Zenite® 5145L WT010 is a 45% glass reinforced, lubricated liquid crystal polymer resin with excellent toughness and a heat deflection temperature of 290°C.Celenese acquired the Zenite product line..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
HDT/A; ISO 75-1/2
Akro-Plastic Akromid® T1 GF 40 9 (3499) PPA Dry, 40% Glass Filled
The new AKROMID® T is characterized primarily by high heat resistance and the lowest moisture absorption of the three PA grades, making it particularly well-suited in the automotive sector for high..
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1, -2
Celanese VECTRA S540 LCP, 40% Mineral Reinforced
40% mineral filled grade, low warpage high flow.Information provided by Celanese
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ISO 75-1/-2
DSM Stanyl® TW200F3 (DAM) Nylon 46 15% Glass Reinforced, Heat Stabilized (North America)
Information provided by DSM Engineering Plastics.
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP VERTON UX03320 PPA (Asia Pacific)
VERTON* UX03320 is a compound based on Polyphthalamide resin containing Long Glass.
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Post Baked; ASTM D648A
Sumitomo Bakelite North America Epiall® 1960B-1 Mineral and Glass Filled Electrical Encapsulation Grade Epoxy
Epiall 1960B-1 is a mineral and short fiberglass filled epoxy compound, formulated for the encapsulation of passive electronic devices.Information provided by Sumitomo Bakelite North America, Inc.
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ASTM D648
Resinoid 7201 Phenolic Molding, Glass Reinforced
Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® A-1625 HS Polyphthalamide (PPA)  (Unverified Data**)
Amodel A-1625 HS is a 25% carbon and glass-reinforced, heat-stabilized grade of polyphthalamide (PPA). It is formulated for applications requiring the dissipation of static charge. This material is ..