Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 536 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
Quadrant EPP Duratron® PAI T4203 PAI, unfilled, extruded (ISO Data)
Duratron T4203 PAI offers the best toughness and impact strength of all Duratron PAI grades. This extruded Duratron PAI grade is very popular for precision parts in high-tech equipment. In addition,..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
Quadrant EPP Duratron® PAI T4501 PAI + graphite + PTFE, compression moulded (ISO Data)
Compression moulded Duratron T4501 PAI is similar in composition to Duratron T4301 PAI, and is selected when larger shapes are required Very high maximum allowable service temperature in air (250°C..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
LATI LATILUB 88/50-20GRT K/10 PEEK Based, 10% Carbon Fiber Reinforced, 20% Graphite and PTFE Self Lubricating Plastic
Latilub self-lubricating plastic materials are designed to replace metals in applications such as gears, bushings, cams, slides, etc., for which, besides their intrinsic properties (moldability, low..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Annealed; ISO 75-2/A
PolyOne Edgetek® AM-35GF/000 FR NH Polyphthalamide (PPA)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Unannealed; ASTM D648
Solvay Specialty Polymers Torlon® 4275 Polyamide-imide (PAI)  (Unverified Data**)
Torlon 4275 is a wear-resistant grade of polyamide-imide (PAI). This grade offers an excellent balance of mechanical properties and wear resistance. It offers high tensile strength and modulus with ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Lehmann & Voss LUVOCOM® 19-7221/OR Polyamide 46, with glass fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automot..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Lehmann & Voss LUVOCOM® 19-7312/GN Polyamide 46, with glass fiber
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Highly dimensionally stable at elevated temperatures.Gear parts for automot..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
LATI Laramid K/40 HM PPA, 40% Carbon Fiber Reinforced
Semi-aromatic polyamide (PPA) based compound. Carbon fiber. High tensile modulus. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP LUBRICOMP UFL36AS PPA (Europe-Africa-Middle East)
LNP* LUBRICOMP* UFL36AS is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized.
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP Lubricomp UFL36ASP PPA (Europe-Africa-Middle East)
LNP* LUBRICOMP* UFL36ASP is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features include Internally Lubricated, Heat Stabilized.This data was supplied by SABIC-IP f..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® AE-1133 Polyphthalamide (PPA), 33% Glass Fiber
Amodel® AE-1133 is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) designed to work in the modern automotive electrical environment. It has a high heat deflection temperature, high ..
Deflection Temperature at 1.8 MPa (264 psi) >= 280 °C
>= 536 °F
ASTM D648A
Sumitomo Bakelite North America 52-70-70-VO-P Short-Glass Reinforced Diallyl Phthalate
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Conforms with the requirements of ASTM D5948 Type..
Deflection Temperature at 1.8 MPa (264 psi) >= 280 °C
>= 536 °F
Post Baked; ASTM D648A
Sumitomo Bakelite North America E 2748-9641D Short Glass Fiber Reinforced Epoxy
E 2748-9641D is a mineral and short fiberglass filled epoxy molding compound.Information provided by Sumitomo Bak North America, Inc.
Deflection Temperature at 1.8 MPa (264 psi) >= 280 °C
>= 536 °F
Post Baked; ASTM D648A
Sumitomo Bakelite North America EM 7302LD-2 Long Glass Fiber Reinforced Epoxy
EM 7302LD-2 is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirabl..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
As Molded; ASTM D648A
Sumitomo Bakelite North America Epiall® 1904B-1 Short Glass Fiber Reinforced Epoxy
Epiall 1904B-1 is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Amodel® A-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, high flexural modulus and high tensile strength. Excellent creep resist..
Deflection Temperature at 1.8 MPa (264 psi) >= 280 °C
>= 536 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP LF006E PEEK (Europe-Africa-Middle East)
LNP* THERMOCOMP* LF006E is a compound based on Polyetheretherketone resin containing Glass Fiber. Added features include: Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
SABIC Innovative Plastics LNP THERMOCOMP LX97024 PEEK (Europe-Africa-Middle East)
LNP* LUBRICOMP* LX97024 is a compound based on Polyetheretherketone containing Glass Fiber, PTFE. Added features include: Internally Lubricated, Easy Molding.
Deflection Temperature at 1.8 MPa (264 psi) >= 280 °C
>= 536 °F
post baked; ASTM D648
Sumitomo Bakelite North America 52-40-40-P Long-Glass Reinforced Diallyl Phthalate
Ortho Resin Isomer (DAP). Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type GDI-30F..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT2V-3H LF PA*-GF30
Grivory TH2V-3H LF is a glass fiber reinforced (30%), PTFE modified engineering thermoplastic based on semi-crystalline partially aromatic copolyamide. Polymer designation acc. ISO: PA6T/66 Polymer ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT2V-3H PA6T/66-GF30
Product description: Grivory HT2V-3H is a 30 % glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamde. Polymer designation acc. to ISO: ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
EMS-Grivory Grivory® HTV-3H1 black 9205 PA6T/6I-GF30
Product description: Grivory HTV-3H1 black 9205 is a 30% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Acc. to ISO: PA 6T/6I...
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
E-Polymers SEPAZ® V330HS 30% Glass Fiber Reinforced Heat Stabilized PPA
Polyphthal Amide Resin (High Temperature Nylon): SEPAZ PPA is a unique semi-crystalline engineering plastic that bridges the cost-performance gap between traditional engineering thermoplastics and s..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ISO 75-1/-2
EMS-Grivory Grivory® HT1V-45 HY black 9205 PA6T/6I-GF45
Product description: Grivory HT1V-45 HY black 9205 is a 45% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. Grivory HT1V-45 HY ..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK)  (discontinued **)
Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
Plenco 7552 Phenolic, Nodular, Transfer Molded
PLENCO 07552 is a glass fiber reinforced novolac phenolic molding compound, exhibiting superior dimensional stability, good impact strength, and good electrical properties. Type ASTM 5948 MFH. UL re..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
As Molded; ASTM D648A
Sumitomo Bakelite North America Epiall® 1914A Short Glass Fiber Reinforced Epoxy
Epiall 1914A is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties.Information provided by..
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
E-Polymers SEPAZ® C130HS 30% Glass Fiber Reinforced High Temperature Stabilized LCP Resin
Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding ..