Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Packaging 2210 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Packaging 2797 Polyvinyl Chloride, Rigid (PVC, Rigid) Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C @Thickness 3.18 mm |
142 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
PolyOne Geon™ Vinyl Rigid Extrusion 87717 Polyvinyl Chloride, Rigid (PVC, Rigid) The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-01 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-182 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 7701 Graphite Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-199 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 195A Medium Neutral Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-393 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 110D Medium Dark Pewter Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-394 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 102E Medium Oak Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-438 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 167 Ebony Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-447 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 9902 Very Dark Gray Applications: Interior trimCenter consolesFuse panelsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-489 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, 101E Lite Oak Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-00 14% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products HP514-00UV 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Natural Applications: Glove box binInterior trimSteering column trimConsolesAir ducts - distributionInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 - 76.7 °C | 142 - 170 °F | Average value: 67.1 °C Grade Count:11 |
Overview of materials for PVC, Transparent This property data is a summary of similar materials in the MatWeb database for the category "PVC, Transparent". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ISO 75A-1, -2 |
LyondellBasell Hostacomâ„¢ RTA3184 Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ RTA3184 medium melt flow, 1,300 MPa flexural modulus, low level glass-reinforced, colorable, interior trim grade thermoplastic elastomeric olefin (TEO) resin is modified .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ASTM D648 |
Techmer ES Elastoblend® PA6 IM 7040 MB Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation pro.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ASTM D648 |
Techmer ES Elastoblend® PA6 IM 7050 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier, Nucleating Agent and LubricantFeatures: Heat Stabilized, Impact Modified, Nucleated and LubricatedInformation pro.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
Lubrizol ESTALOC® 59104 Ester-Type, Reinforced Engineering Thermoplastic Features: Fast cycling, dimensional stability, durability, aesthetics, low temperature impactUses: Injection Molding Available in Americas and AsiaInformation provided by Lubrizol |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
Ensinger Tecamid® 6/12 Nylon (PA612) Type 6/12 has lower moisture absorption rates than nylon 6/6, hence superior dimensional stability.Information provided by Ensinger, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Copolymer CP0437W40L1 Wollastonite Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Homopolymer HP0334M10L Mica Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Homopolymer HP0336W10L1 Wollastonite Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Copolymer CP0436M20L Mica Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Copolymer CP0436T40L Talc Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | |
Aclo Accutech Polypropylene Homopolymer HP0339W10L Wollastonite Reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products CC20P100-01 20% Calcium Carbonate Reinforced Polypropylene, Black Applications: ElectronicsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D-648 |
Chevron Phillips K-Resin® KR03BR SBC
(discontinued **) K-Resin® Styrene-Butadiene Copolymer (SBC)Applications:BottlesMolded boxes and containersMedical devicesPortion packagesBlister packagingFeatures:Good stiffnessGood formabilityGood toughnessExcelle.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | Unannealed; ISO 75-2/Af |
Styron INSPIRE™ TF7000 ES Natural Performance Polymer INSPIRE* TF7000 ES Natural Performance Polymer DA™ is a very high stiffness (2400 MPa) TPO designed for instrument panel upper and lower components, as well as other interior trim applications wher.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 61.1 °C | 142 °F | ASTM D648 |
RheTech Products CC20P100-00 20% Calcium Carbonate Reinforced Polypropylene, Natural Applications: ElectronicsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products. |