- Polymer Property : Thermal Conductivity = 107 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 107 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K | 107 BTU-in/hr-ft²-°F | |
| Eagle Brass 305 Austenitic Stainless Steel, 1/2 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
| Thermal Conductivity | 15.4 W/m-K | 107 BTU-in/hr-ft²-°F | |
| Eagle Brass 305 Austenitic Stainless Steel, 1/4 Hardened Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
| Thermal Conductivity | 15.4 W/m-K | 107 BTU-in/hr-ft²-°F | |
| Eagle Brass 305 Austenitic Stainless Steel, Annealed Type 305 is a chromium nickel stainless steel that can be spun and deep drawn more easily due to an increased nickel content that decreases work hardening. It is nonmagnetic under most conditions. .. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 15.4 W/m-K @Temperature 200 °C |
107 BTU-in/hr-ft²-°F @Temperature 392 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||