- Polymer Property : Thermal Conductivity = 132 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 132 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 19.0 W/m-K @Temperature 85.0 °C |
132 BTU-in/hr-ft²-°F @Temperature 185 °F |
|
| Indium Corp. Indalloy® 281 Bi-Sn Solder Alloy Good low melting point solder for electronics assembly of for applications where Cd and Pb are to be avoided, and for thermo-electric applications. Shear rate sensitive.Information provided by the m.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | Perpendicular to pressing direction |
| Momentive Performance Materials HBT Hot-Pressed Boron Nitride Hot-pressed BN is compacted at temperatures up to 2000°C and pressures up to 2000 psi to form a dense, strong engineering material that is easily machined. It is available in standard and custom.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 500 °C |
132 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 500 °C |
132 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 500 °C |
132 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 500 °C |
132 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| CeramTec SL 303 Silicon Nitride, SiAION+SiC SL 303 is a silicon nitride ceramic. Silicon nitrides are ideal for components working under mechanical loads and engine parts, even and especially at elevated temperatures. Their property profile i.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| Bohler-Uddeholm BÖHLER S400(M7) High Speed Steel Description: High alloyed molybdenum high speed steel with good resistance and high toughness.Applications: Taps, twist drills, reamers, milling tools, broaches tools, cold extrusion dies.Standards:.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Plate > 0.1875" Duplex Stainless Steel, UNS S31803 Ferromagnetic. The AL 2205 alloy is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly improved the corrosion resistance of the alloy; especially in the welded c.. |
|||
| Thermal Conductivity | 19.0 W/m-K | 132 BTU-in/hr-ft²-°F | |
| ATI Allegheny Ludlum AL 2205™ Duplex Stainless Steel, Sheet and Strip < 0.1875", UNS S31803 Ferromagnetic. The AL 2205 alloy is a nitrogen-enhanced duplex stainless steel alloy. The nitrogen serves to significantly improved the corrosion resistance of the alloy; especially in the welded c.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 - 20.5 W/m-K @Temperature 100 - 100 °C |
132 - 142 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F |
Average value: 19.5 W/m-K Grade Count:3 |
| Overview of materials for Epoxy, Cast, Metal Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Cast, Aluminum Filled". Each property range of values reported is minimum and maximum values of a.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 19.0 W/m-K @Temperature 400 °C |
132 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||