- Polymer Property : Thermal Conductivity = 14.8 W/m-K
Polymer Property : Thermal Conductivity = 14.8 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 0% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 10% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 20% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 3.2 mm bright annealed sheet The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, 40% cold work The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and .. |
|||
| Thermal Conductivity | 14.8 W/m-K | 103 BTU-in/hr-ft²-°F | |
| ATI Allegheny Ludlum AL 600™ Nickel-Base Alloy, UNS N06600 Allegheny Ludlum is a nickel-chromium alloy designed for use from cryogenic to elevated temperatures in the range of 1093 degrees Celsius. AL 600 alloy is non-magnetic and readily weldable. The al.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 0% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes Hastelloy® B-3® alloy, heat treated at 1065°C, rapid quenched The attributes of Corrosion-Resistant HASTELLOY® alloys include high resistance to uniform attack, outstanding localized corrosion resistance, excellent stress corrosion cracking resistance, and ea.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 20.0 °C |
103 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
| Schmolz + Bickenbach UGIMA 304/304L® Stainless Steel Bar Description: 304/304L UGIMA® is the next generation of improved high machinability grades from Ugitech. The UGIMA® grades have redefined high machinability stainless steels, showing improvements o.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 300 °C |
103 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal gall.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 0.000 - 100 °C |
103 BTU-in/hr-ft²-°F @Temperature 32.0 - 212 °F |
|
| HP Alloys HPA COBALT Alloy 6B, Wear Resistant, (Co-Cr-W) (UNS R30016) Cobalt 6B is a cobalt based chromium, tungsten alloy for wear environments where seizing, galling and abrasion are present. 6B is resistant to seizing and galling and with its low coefficient of fri.. |
|||
| Thermal Conductivity | 14.8 W/m-K @Temperature 0.000 - 100 °C |
103 BTU-in/hr-ft²-°F @Temperature 32.0 - 212 °F |
|
| HP Alloys HPA COBALT Alloy 6BH, Wear Resistant, (Co-Cr-W) (UNS R30016) Cobalt 6BH is the same composition of Cobalt 6B, except the material is hot rolled and then age hardened. The direct age-hardening after hot rolling provides the maximum hardness and wear resistance.. |
|||