Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 22.3 W/m-K @Temperature 500 °C |
155 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Outokumpu 4724 High Temperature Ferritic Stainless Steel Truly stainless high temperature grade with 13% chromium. Not critical in terms of embrittlement.Applications: Mostly used in high temperature applications with sulphurous atmospheres and/or low te.. |
|||
Thermal Conductivity | 22.3 W/m-K @Temperature 500 °C |
155 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
Outokumpu 4742 High Temperature Ferritic Stainless Steel Good scaling resistance and can be subjected to reducing sulphur environments without risk. Subject to 475°C embrittlement and grain coarsening at temperatures above 950°C. s-phase may form afte.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 20% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, plate, 8000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, plate, 16000 hours exposure at 760°C (1400°F) Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 20% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 30% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 50% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 700 °C |
155 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Thermal Conductivity | 22.4 W/m-K @Temperature 600 °C |
155 BTU-in/hr-ft²-°F @Temperature 1110 °F |
|
Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |