- Polymer Property : Thermal Conductivity = 167 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 167 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | |
| MarkeTech AO 98 Aluminum Oxide Ceramic Substrate, 98% Purity Data provided by the supplier, MarkeTech International.Substrate Specs: Maximum dimensions 4.0 x 6.0 in.. Thickness 0.12-0.60 in. Surface roughness 0.3 µm as fired; 0.075 µm lapped; 0.025 Â.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| CeramTec B 601 Alumina, 98.5% Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | ASTM-C408 |
| CeramTec Rubalit® 708 Alumina, 96% Based on 96% aluminum oxide, Rubalit® 708 was developed specifically for making heavy-duty resistors and miniature metal layer resistors. Because of its outstanding strength, this same material is .. |
|||
| Thermal Conductivity | 24.0 W/m-K | 167 BTU-in/hr-ft²-°F | DIN EN 821-2 / ASTM-C408 |
| CeramTec Rubalit® 708S Alumina, 96% Rubalit® 708S (96%) is an alumina that features high strength and thermal conductivity. It provides outstanding results when used on commercially available thick-film pastes and metallization syste.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 199 °C |
167 BTU-in/hr-ft²-°F @Temperature 390 °F |
hardened and tempered to 350 HB |
| Bohler-Uddeholm BÖHLER RAMAX® HH Modified 420F Chromium alloyed steelTypical applications for Ramax® HH are: holders and bolsters for plastic molds, plastic and rubber molds with low requirements on polishability, and dies for plastic extrusion.. |
|||
| Thermal Conductivity | 24.1 W/m-K | 167 BTU-in/hr-ft²-°F | |
| ATI Allegheny Ludlum AL 400™ Nickel-Base Alloy, Hot Rolled Plate, UNS N04400 Moderately to faintly magnetic at room temperature. Allegheny Ludlum AL 400 alloy is a ductile nickel-copper alloy with resistance to a variety of corrosive conditions. The alloy is most frequentl.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 20.0 - 100 °C |
167 BTU-in/hr-ft²-°F @Temperature 68.0 - 212 °F |
ASTM-C408 |
| CeramTec CeramCool® Rubalit® 708 Alumina, 96% CeramCool® is a metallized ceramic heat-sink for high power applications demonstrated by high power LED-systems. CeramCool® material characteristics: electrical insulation, high volume resistivit.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 40% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 24.0 W/m-K @Temperature 700 °C |
167 BTU-in/hr-ft²-°F @Temperature 1290 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||