- Polymer Property : Thermal Conductivity = 20.8 W/m-K
Polymer Property : Thermal Conductivity = 20.8 W/m-K Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K | 144 BTU-in/hr-ft²-°F | |
| SGL Carbon Group EK 3205 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
| Thermal Conductivity | 20.8 W/m-K | 144 BTU-in/hr-ft²-°F | |
| SGL Carbon Group EK 3235 Carbon Graphite Good mechanical strength, good sliding properties, high temperature resistance, high thermal shock resistance, low wettability, high corrosion resistance, high thermal conductivity, high purity, and.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 593 °C |
144 BTU-in/hr-ft²-°F @Temperature 1100 °F |
|
| ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| Thermal Conductivity | 20.8 W/m-K @Temperature 500 °C |
144 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||