- Polymer Property : Thermal Conductivity = 135 BTU-in/hr-ft²-°F
Polymer Property : Thermal Conductivity = 135 BTU-in/hr-ft²-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.4 W/m-K @Temperature 400 °C |
135 BTU-in/hr-ft²-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Thermal Conductivity | 19.5 W/m-K @Temperature 500 °C |
135 BTU-in/hr-ft²-°F @Temperature 932 °F |
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||