Polymer Property : Thermal Conductivity = 21.5 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 204Â°C (400Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 316Â°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 427Â°C (800Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 538Â°C (1000Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 649Â°C (1200Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 760Â°C (1400Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 871Â°C (1600Â°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, aged 1000 hours at 982Â°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 500 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
Haynes UltimetÂ® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Thermal Conductivity	21.5 W/m-K @Temperature 800 Â°C	149 BTU-in/hr-ftÂ²-Â°F @Temperature 1470 Â°F
Haynes 625SQÂ® Nickel Alloy Sheet Haynes 625SQ alloy is a solid-solution strengthened superalloy. It is a modification of Haynes 625 alloy designed to enhance resistance to fatigue at temperatures up to approximately 1200Â°F (649Â..
Thermal Conductivity	21.5 W/m-K @Temperature 399 °C	149 BTU-in/hr-ft²-°F @Temperature 750 °F
EDRO UltraChem® #15 Precipitation Hardening Stainless Mold Steel Ultrachem® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by: exceptional corrosion resistance, uniform hardness in all dimensions, ..
Thermal Conductivity	21.5 W/m-K @Temperature 399 °C	149 BTU-in/hr-ft²-°F @Temperature 750 °F
EDRO UltraChem® ESR #16 Precipitation Hardening Stainless Mold Steel Ultrachem ESR® is a chromium-nickel precipitation-hardening stainless steel, a modified PH alloy grade, which is characterized by exceptional polishability, exceptional corrosion resistance, unifor..
Thermal Conductivity	21.5 W/m-K @Temperature 200 °C	149 BTU-in/hr-ft²-°F @Temperature 392 °F
Assab Steels ASSAB XW-5 Cold Work Steel ASSAB XW-5 is a high-carbon, high chromium tool steel alloyed with tungsten, characterized by:High wear resistanceHigh compressive strengthHigh surface hardness after hardeningGood through-hardening..