- Polymer Property : Specific Heat Capacity = 0.125 BTU/lb-°F
Polymer Property : Specific Heat Capacity = 0.125 BTU/lb-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.525 J/g-°C @Temperature 400 °C |
0.125 BTU/lb-°F @Temperature 752 °F |
|
| Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, 1.6 mm sheet, aged 128 hours at 815°C (1500°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.523 J/g-°C @Temperature 570 °C |
0.125 BTU/lb-°F @Temperature 1060 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| Specific Heat Capacity | 0.521 J/g-°C @Temperature 300 °C |
0.125 BTU/lb-°F @Temperature 572 °F |
|
| Special Metals NIMONIC® alloy 91 Ni-Cr-Co Alloy NIMONIC® alloy 91 is a wrought nickel-chromium-cobalt based alloy strengthened by additions of aluminum and titanium.This alloy is a modification of NIMONIC alloy 90, but has an increased chromium .. |
|||