Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 2880 - 4320 min @Temperature 25.0 °C |
48.0 - 72.0 hour @Temperature 77.0 °F |
Complete Cure Cycle |
Northstar Polymers MPP-D80B Rigid Polyurethane MPP-D80B has a high load-bearing property at hardness 80 D Durometer. This material has a relatively slow curing pattern. Whereas many polyurethane formulations of this hardness cure very fast thus.. |
|||
Cure Time | 2880 min @Temperature 25.0 °C |
48.0 hour @Temperature 77.0 °F |
Complete Cure Cycle |
Northstar Polymers MPS-M23B Room-Temperature Curable Microcellular Foam This foam polyurethane formulation is designed to yield closed-cell microcellular foam by either hand-mixing or machine casting method at room temperature. The components are liquid at room temperat.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21NDFG Two component epoxy compound for high performance applications Product Description: Master Bond EP21NDFG is a two component, room temperature curing epoxy adhesive featuring outstanding physical properties, easy processing and a non-drip, paste-like consistency.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21NDLO Low Outgassing, Room Temperature Curing Two Component Epoxy Master Bond EP21ND-LO is a two component, room temperature curing epoxy system for bonding, sealing and coating featuring outstanding physical properties. EP21ND-LO has a convenient one to one mix r.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound Product Description: Master Bond EP21TDC-2ND is a two component highly flexible epoxy resin system for high performance bonding, sealing and coating with a non-drip consistency. It has a forgiving o.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21TDCHT-LO Room Temperature Curing, Toughened Two Component Epoxy Master Bond Polymer Adhesive EP21TDCHT-LO is a two component epoxy adhesive formulated to cure at room temperature or more rapidly at elevated temperatures, with a very forgiving and convenient one .. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21TDCHTND Versatile, toughened two component epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDCHTND is a two component epoxy adhesive, sealant and coating featuring high performance, versatility and exceptional user friendliness. It has a very forgiving.. |
|||
Cure Time | 2880 - 3600 min @Temperature 23.0 °C |
48.0 - 60.0 hour @Temperature 73.4 °F |
|
Master Bond EP21TPND Non Drip Polysulfide Based Two Component Adhesive System Master Bond Polymer Adhesive EP21TPND is a two component polysulfide/epoxy based adhesive/sealant formulated to cure at room temperature or more rapidly at elevated temperatures, with a 100 to 100 m.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP42HT-2Med Epoxy Meets USP Class VI Requirements Description: Master Bond Polymer System EP42HT-2Med is a room temperature curable two component epoxy, adhesive, sealant, coating and casting material featuring high temperature resistance along wit.. |
|||
Cure Time | 2880 min @Temperature 25.0 °C |
48.0 hour @Temperature 77.0 °F |
|
Tra-Con Tra-Bond 342-3.5 Room Temperature Cure Epoxy Adhesive TRA-BOND 342-3.5 room temperature curing epoxy adhesive is designed for applications which require outstanding thermal shock properties. This adhesive may be used to bond semi-porous materials such .. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21FRNS-2 Two Component, Flame Resistant Epoxy System Master Bond Polymer System EP21FRNS-2 is a two component, room temperature curing, flame retardant compound for potting, encapsulating and casting. Particularly noteworthy are its low smoke generati.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.0 °C |
48.0 - 72.0 hour @Temperature 73.4 °F |
|
Master Bond EP30M3LV Electrically Insulative, Low Viscosity Two Component Epoxy Master Bond Polymer System EP30M3LV is a lower viscosity, two component epoxy system for high performance bonding, sealing and encapsulation. It is formulated to cure at ambient temperatures or mor.. |
|||
Cure Time | 2880 min @Temperature 16.0 °C |
48.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
Cure Time | 2880 min @Temperature 16.0 °C |
48.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 2880 min @Temperature 25.0 °C |
48.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 2880 min @Temperature 16.0 °C |
48.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
Cure Time | 2880 min @Temperature 25.0 °C |
48.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC S2 Ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% soli.. |
|||
Cure Time | 2880 min @Temperature 25.0 °C |
48.0 hour @Temperature 77.0 °F |
|
Epoxyset Epoxiohm EO-21M-5 Electrically Conductive Epoxy Adhesive EO-21M-5 is an electrically conductive & thermally conductive, silver filled epoxy adhesive. This two component system is designed to be cured at room temperature or the cure can be accelerated by e.. |
|||
Cure Time | 2880 min @Temperature 10.0 °C |
48.0 hour @Temperature 50.0 °F |
Full Chemical |
Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th.. |
|||
Cure Time | 2880 min @Temperature 10.0 °C |
48.0 hour @Temperature 50.0 °F |
Full Load |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Cure Time | 2880 min @Temperature 22.0 °C |
48.0 hour @Temperature 71.6 °F |
|
Dow Corning 3-4130 DIELECTRIC GEL KIT Two-part, clear, heat cure, low extractables.Information provided by Dow Corning |
|||
Cure Time | 2880 min @Temperature 22.2 °C |
48.0 hour @Temperature 72.0 °F |
>2 Hour Air Set Required Prior to Curing |
Aremco Corr-Paint™ CP2050-XX High Temperature Protective Coating Epoxy-Phenolic, Glass Fiber Filled This epoxy and urethane based coating is used for producing corrosion and wear resistant barriers to 500 °F. Typical applications include tanks, pipelines, boilers, precipitators, scrubbers, bag ho.. |
|||
Cure Time | 2880 min @Temperature 22.2 °C |
48.0 hour @Temperature 72.0 °F |
>8 Hour Air Set Required Prior to Curing |
Aremco Corr-Paint™ CP2060 High Temperature Protective Coating Novolac-Epoxy, Silicon Carbide Filled This epoxy and urethane based coating is used for producing corrosion and wear resistant barriers to 500 °F. Typical applications include tanks, pipelines, boilers, precipitators, scrubbers, bag ho.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP21TDC-2LO Two component, highly flexibilized epoxy resin compound Product Description: Master Bond Polymer System EP21TDC-2LO is a two component, highly flexible epoxy resin compound for high performance bonding, sealing, coating, and encapsulation. It is formulat.. |
|||
Cure Time | 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
|
Master Bond EP33LV Epoxy Has Dimensional Stability and Machinability Description: Master Bond EP33LV is a two part, room temperature curing epoxy system used for bonding, sealing and coating featuring high temperature resistance, good dimensional stability and very g.. |