Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 480 - 960 min @Temperature 25.0 °C |
8.00 - 16.0 hour @Temperature 77.0 °F |
|
Resinlab® EP1285HD-16 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
De-mold Time |
Northstar Polymers MPA-A30B Mold-Making Resin MPA-A30B is a room-temperature-cure liquid castable polyurethane system. This ether-base polyurethane system is used in applications such as mold-making, prototyping, production of cast parts, pott.. |
|||
Cure Time | 480 - 540 min @Temperature 25.0 °C |
8.00 - 9.00 hour @Temperature 77.0 °F |
De-mold Time |
Northstar Polymers MPP-D80B Rigid Polyurethane MPP-D80B has a high load-bearing property at hardness 80 D Durometer. This material has a relatively slow curing pattern. Whereas many polyurethane formulations of this hardness cure very fast thus.. |
|||
Cure Time | 480 min @Temperature 82.2 °C |
8.00 hour @Temperature 180 °F |
Complete Cure Cycle |
Northstar Polymers MSB-D60A High Performance Polyurethane Cast Elastomer System This is an Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires some lord bearing, high tensile strength, cut/tear res.. |
|||
Cure Time | 480 min @Temperature 82.2 °C |
8.00 hour @Temperature 180 °F |
Complete Cure Cycle |
Northstar Polymers MSB-M25F Microcellular Foam based on High Performance Polyester Polyurethane This high performance polyester microcellular foam system is one of a family of polymer systems developed by Northstar Polymers for demanding work environments. Urethane foams molded with this syste.. |
|||
Cure Time | 480 - 960 min @Temperature 71.1 - 82.2 °C |
8.00 - 16.0 hour @Temperature 160 - 180 °F |
Complete Cure Cycle |
Northstar Polymers MSN-V40A Polyester Base Low-Rebound Impact/Vibration Dampening Gel This polyurethane casting material is developed for applications that require Shore OO 40 range casting material with vibration dampening property and higher strength than standard polyurethane gel .. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
De-mold Time |
Northstar Polymers GK-7 Low Viscosity Polyurethane Gel Cast This material is formulated for production of thin polyurethane gel film or parts. The low viscosity property of the mixed component enables the user to cast this into a thin layer without entrappi.. |
|||
Cure Time | 480 min @Temperature 60.0 °C |
8.00 hour @Temperature 140 °F |
|
Tra-Con Tra-Bond 724-17 Polyurethane Adhesive TRA-BOND 724-17 premixed and frozen, polyurethane adhesive is designed for good adhesion, providing strong resilient bonds to a wide variety of substrates, including aluminum, solder, nylon, mylar a.. |
|||
Cure Time | 480 - 960 min @Temperature 25.0 °C |
8.00 - 16.0 hour @Temperature 77.0 °F |
|
Trelleborg Emerson & Cuming Eccobond® 1309 General Purpose Catalyst Emerson & Cuming 1309 Eccobond® General Purpose CatalystFaster curing version of 9. Very fast room temperature curing, low viscosity, general purpose. Short working life. Imparts excellent chemical.. |
|||
Cure Time | 480 - 960 min @Temperature 25.0 °C |
8.00 - 16.0 hour @Temperature 77.0 °F |
|
Trelleborg Emerson & Cuming Eccobond® 24 LV General Purpose Catalyst Emerson & Cuming 24 LV Eccobond® General Purpose CatalystFaster curing, shorter working life version of 23 LV. Recommended for small mass castings due to higher exotherm. Cure Type: Room Temp or He.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
|
Tra-Con Tra-Bond 868-3N1 Room Temperature Cure Adhesive TRA-BOND 868-3N1 room temperature cure adhesive provides strong bonds to difficult-to-bond metals, such as gold, silver, copper, brass, and solder.Information provided by Tra-Con Inc. |
|||
Cure Time | 480 min @Temperature 4.00 °C |
8.00 hour @Temperature 39.2 °F |
Full Chemical |
Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control Description: ARC 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patc.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
Cure Time | 480 min @Temperature 16.0 °C |
8.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC HT-T Spark Testable High Temperature Trowelable Abrasion Control Compound An advanced ceramic composite formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. This system is a high viscosity composite that is applied b.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
Cure Time | 480 min @Temperature 10.0 °C |
8.00 hour @Temperature 50.0 °F |
Full Load |
Chesterton ARC NVE SYSTEM Vinyl Ester Lining Description: ARC NVE is a high performance, quartz reinforced, three-component, modified novolac vinyl ester lining capable of being applied to horizontal and vertical surfaces. The NVE system kit i.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Tack Free |
Chesterton MRS S4+ Metal Rebuilding System An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375 microns (15 .. |
|||
Cure Time | 480 min @Temperature 80.0 °C |
8.00 hour @Temperature 176 °F |
|
Cytec EN-11 (Conap) Casting, Potting, and Molding Compound High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable.. |
|||
Cure Time | 480 - 720 min @Temperature 25.0 °C |
8.00 - 12.0 hour @Temperature 77.0 °F |
|
Epoxyset Epoxiohm EO-30FST Electrically Conductive Epoxy Adhesive EO-30-FST is two part, fast cure, silver filled, and high electrical conductivity epoxy adhesive. Both components are silver filled permitting a simple 1:1 mix ratio by weight. It has smooth creamy .. |
|||
Cure Time | 480 - 660 min @Temperature 22.0 °C |
8.00 - 11.0 hour @Temperature 71.6 °F |
|
Dow Corning 3-4241 DIELECTRIC TOUGH GEL KIT Two-part, translucent green, RT or heat cure, UV indicator, long working time, tough primerless chemical adhesion, UL 94 V-1 flammability classification.Information provided by Dow Corning |
|||
Cure Time | 480 min @Temperature 24.0 °C |
8.00 hour @Temperature 75.2 °F |
handling time |
BCC Products BC 9020 Silicone RTV Rubber BC 9020 is a violet colored, two-component, flowable compound that regardless of thickness or confinement, cures at room temperature. The cured rubber is high strength and high tear with good elonga.. |
|||
Cure Time | 480 - 960 min @Temperature 25.0 °C |
8.00 - 16.0 hour @Temperature 77.0 °F |
|
Resinlab® EP1285HD-14 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
Cure Time | 480 min @Temperature 10.0 °C |
8.00 hour @Temperature 50.0 °F |
Full Load |
Chesterton ARC NVE VC Vinyl Ester Sealer Description: ARC NVE VC (Veil Coat) is a two-component, modified epoxy novolac vinyl ester sealer coat formulated for application by brush, roller or spray at 0.15-0.25 mm (0.07-0.010”) wet film th.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Tack Free |
Chesterton ARC S4+ 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375.. |
|||
Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
|
3M AC-250 B-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 B-1/6 is a two-part, polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a thixotropic paste and can be read.. |