Polymer Property : Cure Time = 96.0 hour Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Processing Properties Metric English Comments
Cure Time 5760 - 10100 min

@Temperature 25.0 °C
96.0 - 168 hour

@Temperature 77.0 °F
full cure
Permabond ET5401 Epoxy Resin
PERMABOND® ET5401 is a two-part, 2:1 mixable, semi-flexible toughened no slump epoxy adhesive with good adhesion to a variety of substrates such as wood, metal, ceramics and some plastics and compo..
Cure Time 5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Full
Lord Adhesives Thermosetâ„¢ UR-322 Two Component Urethane Potting Compound
Lord UR-322 is a two component, room temperature curing urethane potting compound. The cured elastomer is soft, flexible and has a very low modulus at temperatures down to -80°C. Cured UR-322 als..
Cure Time 5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Tra-Con Tra-Duct 2956 Low Ion Snap Cure Silver Epoxy Adhesive
TRA-DUCT 2956 is recommended for the bonding and sealing of electronic components where a combination of electrical and mechanical properties are required. This two-part, smooth, paste system of sil..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton ARC 10 Paste grade machinable composite
Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance and corrosion resistance. It is non-sag..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Load
Chesterton ARC 855 Abrasion Control Liquid
Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by..
Cure Time 5760 min

@Temperature 16.0 °C
96.0 hour

@Temperature 60.8 °F
Full Chemical
Chesterton ARC 855 Abrasion Control Liquid
Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton ARC 858 Abrasion resistant rebuilding and faring composite
An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton ARC 897 Fine Grade Sliding Wear Compound
Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound
Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It ..
Cure Time 5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Full Mechanical/Chemical
Chesterton ARC MXHT High temperature severe wear compound
Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness o..
Cure Time 5760 min

@Temperature 16.0 °C
96.0 hour

@Temperature 60.8 °F
Full Chemical
Chesterton ARC S2 Ceramic reinforced erosion resistant coating
Description: An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% soli..
Cure Time 5760 min

@Temperature 16.0 °C
96.0 hour

@Temperature 60.8 °F
Full Chemical
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating
Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat..
Cure Time 5760 min

@Temperature 16.0 °C
96.0 hour

@Temperature 60.8 °F
Full Chemical
Chesterton MRS S2 Metal Rebuilding System
An advanced ceramic composite for the resurfacing and protection of all metal surfaces. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrinking, 100% solids. MRS S2 is..
Cure Time 5760 min

@Temperature 16.0 °C
96.0 hour

@Temperature 60.8 °F
Full Chemical
Chesterton MRS SD4i Metal Rebuilding System
An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri..
Cure Time 5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Full Mechanical
Chesterton ARC HT-S High Temperature Corrosion Resistant Coating
Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with ..
Cure Time 5760 min

@Temperature 25.0 °C
96.0 hour

@Temperature 77.0 °F
Full Chemical
Chesterton ARC HT-S High Temperature Corrosion Resistant Coating
Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with ..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton ARC MX2 High Wear Fine Particle Wear Compound
Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”..
Cure Time 5760 - 11520 min

@Temperature 20.0 °C
96.0 - 192.0 hour

@Temperature 68.0 °F
(4-8 days)
Abatron AboCoat 8501-2/AboCure 8501-2 Clear Epoxy Coating
AboCoat 8501-2 is a clear, light amber resin made of 85% solids. It has a viscosity of 21-23 poises and a weight of 9.3 lbs/gallon. AboCure 8501-2 is a clear, light amber converter made of 85% solid..
Cure Time 5760 - 8640 min

@Temperature 15.556 - 26.667 °C
96.0 - 144 hour

@Temperature 60.001 - 80.001 °F
(4-6 Days)
Abatron AboTar 8607-1 Solventless Tar-Epoxy Compound
AboTar 8607-1 is a 2-part tar-epoxy lower cost system for filling and leveling pot holes and grossly uneven flooring. It can be used neat or with sand or aggregates. Uses: Resurfacing concrete and ..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton MRS 10 Metal Rebuilding System
Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 10..
Cure Time 5760 min

@Temperature 10.0 °C
96.0 hour

@Temperature 50.0 °F
Full Chemical
Chesterton MRS 58 Metal Rebuilding System
An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo..