Processing Properties | Metric | English | Comments |
---|---|---|---|
Drying Temperature | 130 - 150 °C | 266 - 302 °F | |
PolyOne Edgetek® XP9242701 Polyphenylene Sulfide (PPS) Injection Speed: 50 to 80% Holding Time: 3 to 9 sec Injection Time: 1 to 3 sec Cycle Time: 18 to 70 secInformation provided by PolyOne |
|||
Drying Temperature | 130 - 150 °C @Time 10800 sec |
266 - 302 °F @Time 3.00 hour |
|
LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced High thermal conductivity product based on Polyphenylene Sulfide (PPS). Special filler. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Drying Temperature | 130 - 150 °C @Time 10800 sec |
266 - 302 °F @Time 3.00 hour |
|
LATI Latilub 80-10T K/15 PPS, 15% Carbon Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GF33HI 33% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® B GF30 30% Glass Fiber Reinforced PET Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GB30 30% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GF20HI 20% Glass Fiber Reinforced, High Impact PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman VOLOY™ 462 Hybrid Reinforced PBT Alloy Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® A GF50 50% Glass Fiber Reinforced PBT Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET Information provided by A. Schulman. |
|||
Drying Temperature | 130 °C | 266 °F | |
Beijing Chemical Industry KAIFA® 301-G10F PBT Resin 10% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Drying Temperature | 130 °C | 266 °F | |
Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin 30% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Drying Temperature | 130 °C | 266 °F | |
Beijing Chemical Industry KAIFA® HN301-G30 PA6 Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Drying Temperature | 130 - 140 °C | 266 - 284 °F | Temperature can be reduced when using vacuum ovens. |
LATI LARTON G/50 50% Glass Fiber Filled Polyphenylene sulfide (PPS)
(discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex.. |
|||
Drying Temperature | 130 °C | 266 °F | |
Beijing Chemical Industry KAIFA® MN201-G10 Nylon 66 Resin 10% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group) |