Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
Quantum Composites AMC™ 8595 55% Carbon Fiber Reinforced Vinyl Ester SMC AMC™ 8595 is a vinyl ester engineered structural composite molding compound with continuous, unidirectional carbon fibers. It is designed for compression molding of components requiring high struc.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
Quantum Composites QC-8700 63% Glass Fiber Reinforced Vinyl Ester SMC QC-8700 is a vinyl ester engineered structural composite molding compound for compression molding of components requiring high structural strength. It exhibits unusual toughness, and is suggested f.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 149 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 300 °F |
|
Quantum Composites QC-8777 41% Glass Fiber Reinforced Polyester Hybrid SMC QC-8777 is a polyester hybrid engineered structural composite molding compound designed for compression molding of components requiring high structural strength, corrosion resistance and temperature.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
Quantum Composites QC-8816 66% Glass Fiber Reinforced Polyester Hybrid SMC QC-8816 is a polyester hybrid engineered structural composite molding compound reinforced with continuous, unidirectional (0°) glass fibers. It provides high strength, stiffness and fatigue resist.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 mm, Temperature 138 °C |
0.0500 - 0.0833 hour @Thickness 0.250 in, Temperature 280 °F |
|
Quantum Composites QC-8850 43% Glass Fiber Reinforced Polyester Hybrid SMC QC-8850 is a polyester hybrid engineered structural composite molding compound designed for compression molding of components requiring high structural strength. It exhibits unusual toughness, and .. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | handling time with no initiator |
Permabond TA437 Toughened Acrylic Adhesive PERMABOND TA437 is a single component structural acrylic adhesive designed primarily for bonding metals, ferrites and ceramics. The typical fixture time of TA437 when used with Initiator 41 is 30 –.. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | handling time |
Permabond TA4302 Toughened Acrylic Adhesive PERMABOND® TA4302 is a 2-part, 1:1 toughened acrylic adhesive. It can be used to bond a wide variety of materials including metals, plastics, GRP, ceramics, wood and other substrates. It is conveni.. |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | Working time |
ITW Devcon Flex Welderâ„¢ Methacrylate Adhesive FC, Off-White, Black Information provided by ITW Devcon |
|||
Cure Time | 4.00 - 5.00 min | 0.0667 - 0.0833 hour | Working time |
ITW Devcon Metal Welderâ„¢ Methacrylate Adhesive, Grey / Beads Information provided by ITW Devcon |
|||
Cure Time | 3.00 - 5.00 min | 0.0500 - 0.0833 hour | Open Time |
3M 5010 Polyurethane Multi-Purpose Adhesive 3M™ Polyurethane Multi-Purpose Adhesive 5010 is a one component, fast curing adhesive which forms a rigid permanent bond. 3M 5010 bonds to a wide variety of materials including wood, foam panels, f.. |
|||
Cure Time | 3.00 - 5.00 min @Temperature 138 - 138 °C |
0.0500 - 0.0833 hour @Temperature 280 - 280 °F |
Average value: 5.17 min Grade Count:1 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |
|||
Cure Time | 3.00 - 5.00 min @Thickness 6.35 - 6.35 mm |
0.0500 - 0.0833 hour @Thickness 0.250 - 0.250 in |
Average value: 5.17 min Grade Count:1 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |