Polymer Property : Cure Time = 1440 min Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 720 - 1440 min | 12.0 - 24.0 hour | Full cure for handling |
| P & P Technology MS-N Nickel Graphite Conductive Adhesive P & P Technology conductive nickel/graphite adhesive is a one part electrically conductive room temperature curing elastomer. It is supplied as a readily extrudable paste that cures rapidly when exp.. |
|||
| Cure Time | 15.0 - 1440 min @Temperature 57.2 - 100 °C |
0.250 - 24.0 hour @Temperature 135 - 212 °F |
Average value: 434 min Grade Count:17 |
| Overview of materials for Thermoset Polyurethane, Liquid This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Liquid". Each property range of values reported is minimum and maximum values of.. |
|||
| Cure Time | 1.50 - 1440 min | 0.0250 - 24.0 hour | Average value: 372 min Grade Count:32 |
| Overview of materials for Methacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Methacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropri.. |
|||
| Cure Time | 0.750 - 1440 min @Temperature 40.0 - 302 °C |
0.0125 - 24.0 hour @Temperature 104 - 576 °F |
Average value: 81.6 min Grade Count:121 |
| Overview of materials for Epoxy, Electrically Conductive This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Electrically Conductive". Each property range of values reported is minimum and maximum values of.. |
|||
| Cure Time | 1080 - 1440 min @Temperature 25.0 °C |
18.0 - 24.0 hour @Temperature 77.0 °F |
|
| Fibre Glast 1099 Room Temperature Epoxy Surface Coat Safety hardener with fast overnight cure. Low viscosity thins the resin well for best detail reproduction. Can be sanded in 16-18 hours. #1099 is a white, medium viscosity epoxy surface coat that c.. |
|||
| Cure Time | 720 - 1440 min @Temperature 204 - 232 °C |
12.0 - 24.0 hour @Temperature 399 - 450 °F |
Post cure |
| Lord Adhesives Chemlok® 5150 Adhesive LORD Chemlok® 5150 adhesive is a solvent-based adhesive used to bond uncured fluoroelastomers to metal. It can also be used to bond fluoroelastomers with an incorporated cure system to mechanical.. |
|||
| Cure Time | 1080 - 1440 min @Temperature 23.9 °C |
18.0 - 24.0 hour @Temperature 75.0 °F |
85% maximum strength developed within |
| Master Bond EP21TDCNFL Two Component Nickel Conductive Epoxy Adhesive Master Bond Polymer System EP21TDCNFL is a two component, nickel filled, electrically conductive system for high performance bonding and sealing formulated to cure at room temperature or more rapidl.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.0 °C |
12.0 - 24.0 hour @Temperature 73.4 °F |
|
| Master Bond Mastersil 415 One Component Room Temperature Curing, Transparent Silicon Master Bond MasterSil 415 is a ready-to-use, one component high performance silicone elastomer compound for bonding, sealing and protective coatings featuring high transparency. It has a paste consi.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.9 °C |
12.0 - 24.0 hour @Temperature 75.0 °F |
|
| Master Bond X17MED Elastomer Compound for Medical Device Applications Description: Master Bond Polymer System X17MED is a specially formulated one component adhesive specially designed for bonding polyolefins such as polypropylene and polyethylene as well as their man.. |
|||
| Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure Time @ 20ºC |
| Loctite® 3873 1 component acrylic High Conductivity Flexible Adhesive Thermally Conductive BondersLoctite® Thermally Conductive Adhesives eliminate the need for mechanical fasteners and clips, while providing the most efficient thermal transfer between transistors or.. |
|||
| Cure Time | 5.00 - 1440 min | 0.0833 - 24.0 hour | Full Cure |
| Loctite® 5205 Flexible Cure Flange Sealant Anaerobic GasketingLoctite® 5205 Flexible Cure Flange SealantFast curing and flexible, good sealing properties against oil and water/glycol particularly at high temperatures. High viscosity. Recom.. |
|||
| Cure Time | 60.0 - 1440 min | 1.00 - 24.0 hour | Full Cure, Unprimed |
| Loctite® 5205 Flexible Cure Flange Sealant Anaerobic GasketingLoctite® 5205 Flexible Cure Flange SealantFast curing and flexible, good sealing properties against oil and water/glycol particularly at high temperatures. High viscosity. Recom.. |
|||
| Cure Time | 5.00 - 1440 min | 0.0833 - 24.0 hour | Full Cure |
| Loctite® 5206 Flexible Cure Flange Sealant Anaerobic GasketingLoctite® 5206 Flexible Cure Flange SealantSlow curing allows for micro-movement during assembly operations. Good sealing properties against oil and water/glycol. High viscosity... |
|||
| Cure Time | 60.0 - 1440 min | 1.00 - 24.0 hour | Full Cure, Unprimed |
| Loctite® 5206 Flexible Cure Flange Sealant Anaerobic GasketingLoctite® 5206 Flexible Cure Flange SealantSlow curing allows for micro-movement during assembly operations. Good sealing properties against oil and water/glycol. High viscosity... |
|||
| Cure Time | 180 - 1440 min @Temperature 22.0 °C |
3.00 - 24.0 hour @Temperature 71.6 °F |
|
| Dow Corning SLYGARD® 3-6636 SILICONE DIELECTRIC GEL KIT Two-part, transparent, LED encapsulant which is a lower-viscosity version of EG-6301.Information provided by Dow Corning |
|||
| Cure Time | 960 - 1440 min | 16.0 - 24.0 hour | |
| Dow BETAMATE™ 7000/7050 L Epoxy Two component room temperature fast curing polyurethane structural adhesive with high elastic modulus.Information provided by Dow |
|||
| Cure Time | 960 - 1440 min @Temperature 93.3 °C |
16.0 - 24.0 hour @Temperature 200 °F |
|
| Cotronics Duralco™ 122 500°F (260°C) Nickel Filled Adhesive and Casting Epoxy Specially formulated to provide an economical alternative to silver filled electrically conductive epoxies. Applications: for use in applications where highest electrically conductivity not required.. |
|||
| Cure Time | 960 - 1440 min @Temperature 93.3 °C |
16.0 - 24.0 hour @Temperature 200 °F |
|
| Cotronics Duralco™ 128 500°F (260°C) Ceramic Filled Epoxy Ceramic filled, electrically resistant adhesive and potting compound. The ceramic fillers provide both high thermal conductivity and high dielectric strength. Cures at room temperature. Curing ca.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full Cure |
| 3M Scotch-Weld™ DP8010 Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polypropyl.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full Cure |
| 3M Scotch-Weld™ DP8010NS Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8010NS is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of Polyprop.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full cure |
| 3M Scotch-Weld™ DP805 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP805 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
| Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full cure |
| 3M Scotch-Weld™ DP807 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP807 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full cure |
| 3M Scotch-Weld™ DP810 Black Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full cure |
| 3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
| Cure Time | 480 - 1440 min | 8.00 - 24.0 hour | Full cure |
| 3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
| Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure, Unprimed |
| Loctite® 5182 Flexible Cure Anaerobic Sealant Anaerobic GasketingLoctite® 5182 Flexible Cure Anaerobic SealantRecommended Primer: 7649 (N). Typical Use: Robotic application on flanges, seals, covers |
|||
| Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure; Unprimed |
| Loctite® Gasket Eliminator® 510 Flange Sealant Anaerobic GasketingLoctite® 510 High Temperature Rigid Cure Gasket Eliminator® Flange SealantProduct has a temperature range to 400ºF with excellent solvent and chemical resistance. Makes or dre.. |
|||
| Cure Time | 240 - 1440 min | 4.00 - 24.0 hour | Full Cure Time @ 20ºC |
| Loctite® Output™ 383 Acrylic Adhesive Acrylic Bonding Adhesives and Thermally Conductive BondersLoctite® Acrylic Adhesives were developed for bonding applications that require tensile, shear and peel strength combined with maximum impa.. |
|||