Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 15.0 min @Temperature 160 °C |
0.250 hour @Temperature 320 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Black Peroxide Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Temperature 155 °C |
0.250 hour @Temperature 311 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Sulfur Cure Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Temperature 150 °C |
0.250 hour @Temperature 302 °F |
|
Gwent Electronic Materials C2100217D1 Aluminium for PTC paste Aluminium Ink designed to give good ohmic contact on to barium titanate PTC components. This product is particularly good where large volumes of PTC components are being processed in belt furnaces .. |
|||
Cure Time | 15.0 min @Temperature 154 °C |
0.250 hour @Temperature 309 °F |
|
TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-220 (ISAF) Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and m.. |
|||
Cure Time | 15.0 min @Temperature 150 °C |
0.250 hour @Temperature 302 °F |
Minimum Bond Line |
Epoxy Technology EPO-TEK® E2116 Electrically Conductive, Silver Epoxy Product Description: EPO-TEK® E2116 is a two component, silver-filled and stencil printable electrically conductive adhesive for bonding SMDs onto PCB and substrates. Can be used as a “lead-free”.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 19146R025 0.025" (0.635 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Style 1523 FiberglassSide 2: Uncured Silicone RubberInterleave: PolyethyleneAppearance: Black silicone gum and rubber on fiberglass clothT.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 19220R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone Rubber Appearance: Red silicone gum on fiberglass fabricThis data represents typical values for the production material. The data should not be used to w.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 19606R025 0.025" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSubstrate: Prime Coated 1523 FiberglassSide 2: Uncured Silicone RubberInterleave: 0.003" PolyethyleneThis data represents typical values for the .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 49576R015 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone Rubber Appearance: Red silicone gum and rubber on fiberglass clothThis data Represents typical values for the production mat.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 51586R015E 0.015" (0.381 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Cured Silicone RubberSubstrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Interleave: Polyethylene This data represents typical values for the production mat.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 51591R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Cured Silicone Rubber Product Use: Flexible heater insulationAppearance: Red silicone gum on fiberglass with polymer release linersThis data .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 55869R028 0.0295" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PELayer 2: Uncured Silicone RubberLayer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassThis data represents typical values for the production materia.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 56146R028 0.028" (0.711 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 2: Uncured Silicone Rubber Substrate: 1564 Style Fiberglass Side 1: Cured Silicone Rubber Product Use: Flexible heater insulationAppearance: Red si.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon CP-498R Silicone Bulk Compound This data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon CP-PC-2951 Silicone Compound This data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon P30670R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction: Side 1: Uncured Silicone Rubber Substrate: Style 1165 FiberglassAppearance: Red silicone gum on fiberglass with polymer release linersThis data represents typical values for the.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
|
Arlon 51141R020 Silicone Rubber/Fiberglass Laminate Interleave 1: 3 mil PE; Side 1: uncured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave 2: 3 mil PE |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 51271R037 0.037" Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Uncured Silicone RubberInterleave: 2.5 mil PolyethyleneThis data represents typical values for the produ.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 51581B015 0.015" Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave 1: 2.5 mil LDPESide 1: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 2: Uncured Silicone RubberInterleave 2: 2.5 mil LDPEThis data represents typical.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon R33099G028 0.029" (0.737 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone Rubber LayerSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in pl.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon R33991R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberSide 2: Uncured Silicone Rubber This data Represents typical values for the production material. The data should not be used to write, or in place .. |
|||
Cure Time | 15.0 min | 0.250 hour | Air Set prior to curing |
Aremco Glass-Coat™ SGC4000 High Temperature Specialty Coatings Silicone-Glass Silicone-glass-ceramic, gray, low viscosity, scratch resistant coating for stainless steel to 900°F (482°C) |
|||
Cure Time | 15.0 min @Temperature 899 °C |
0.250 hour @Temperature 1650 °F |
|
Aremco Quartz-Coat™ 850 High Temperature Specialty Coatings Inorganic, Glass-Ceramic Filled Glass-ceramic, white reflective coating for glass and quartz to 1500°F (816°F) |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 44426R010 0.010" Cured/Uncured Silicone Rubber Laminate with Fiberglass Substrate Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Cured Silicone RubberSide 2: Uncured Silicone RubberSubstrate: Prime Coated 1165 FiberglassThis data represents typical values for the p.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 44568R016 0.016" (0.406 mm) Cured/Uncured Layers Uncured Rubber with Fiberglass Substrate Design/Construction: Interleave: PolyethyleneSide 1: Uncured Silicone RubberThis data represents typical values for the production material. The data should not be used to write, or in place of, mat.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 44580R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Uncured Silicone RubberAppearance: Red silicone gum on fiberglass clothThis data represents typical values for the production material. The data should not be used to wri.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon 44686W013 0.013" (0.330 mm) Cured/Uncured Silicone Rubber with Fiberglass Substrate Design/Construction:Side 1: Cured Silicone RubberSide 2: Uncured Silicone Rubber UL Recognition: 220°C per UL Card E54153Appearance: White silicone gum on fiberglassThis data represents typical val.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle |
Arlon R35928R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: Polyethylene Side 1, Layer 2: Uncured Silicone RubberSide 1, Layer 1: Cured Silicone Rubber Substrate: Style 7628 Fiberglass Side 2: Cured Silicone RubberAppearance: .. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon 44278R018 0.018" Uncured/Cured/Uncured Silicone Rubber Laminate with Fiberglass Substrate Design/Construction:Interleave 1: LDPESide 1 Layer 2: Uncured Silicone RubberSide 1 Layer 1: Cured Silicone RubberSubstrate: Style 1165 FiberglassSide 2: Uncured Silicone RubberInterleave: LDPEUL.. |
|||
Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
Recommended Cure Cycle |
Arlon R37503G060 0.060" Uncured Fluorosilicone on Release PET Carrier Design/Construction:Interleave: 0.003" PolyethyleneSide 1: Uncured FluorosiliconeCarrier: 0.005" Release PETThis data represents typical values for the production material and should not be used .. |