Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 60.0 min | 1.00 hour | On steel (fixture) |
ND Industries StudGrade® 137 Permanent HT Threadlocker General DescriptionHigh strength, high temperature threadlockers for heavy duty applications. Suitable for most applications where disassembly is not required. |
|||
Cure Time | 60.0 min @Temperature 125 °C |
1.00 hour @Temperature 257 °F |
|
Parker Chomerics Tecknit Teckfip™ HC FIP-E Formed in Place Conductive Elastomer Heat cure compound. Commercial grade FIP compound designed for moderate shielding performance. The Ag/glass particles are very smooth which leads to very low compression set value.Information provid.. |
|||
Cure Time | 60.0 min | 1.00 hour | Ambient |
Reltek BONDiT™ B-536 Adhesive System Key Properties: Very high strength bonding of dissimilar materials.High moisture and solvent resistance.Fast ambient cure with good pot life.Ease of use.Applications: Outstanding adhesive for very h.. |
|||
Cure Time | 60.0 min @Temperature 130 °C |
1.00 hour @Temperature 266 °F |
Oven |
Permabond ES578 Epoxy Resin PERMABOND® ES578 is a single-part heat cured epoxy adhesive with excellent adhesion to metal surfaces, ceramics as well as composite materials. ES578 provides excellent thermal conductivity and bon.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 - 120 min | 1.00 - 2.00 hour | Hand Dry |
Industrial Nanotech Nansulateâ„¢ GP Translucent Insulation Coating Liquid insulation and corrosion protection incorporating Hydro-NM-Oxide, a product of nanotechnology. This grade is for general purpose insulation.NANSULATEâ„¢ liquid applied insulation is a prem.. |
|||
Cure Time | 60.0 min @Temperature 121 °C |
1.00 hour @Temperature 250 °F |
|
Henkel Hysol EA 9628H Film Adhesive First generation, modified epoxy film, high peel strength, good stress, environmental resistance and structural propertiesApplications: Composite Bonding, Metal & Honeycomb BondingData from .060 psf.. |
|||
Cure Time | 60.0 min @Temperature 177 °C |
1.00 hour @Temperature 350 °F |
Heat up rate 10°F/min |
Hexcel® Redux® 219/3-NA Foaming adhesive film The Redux 200 series is a range fo foaming adhesive films presented in sheet form. They expand during the cure cycle to fill gaps and adhere strongly to all parts of the structure with which they co.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.75 PHR Sulfur MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 152 °C |
1.00 hour @Temperature 305 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 70A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 120 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N220 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N774 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min | 1.00 hour | Time to Handling Strength |
3M Scotch-Weld™ DP5003 Structural Adhesive Non-sag and Vertical applicationsInformation provided by 3M |
|||
Cure Time | 60.0 min @Temperature 232 °C |
1.00 hour @Temperature 450 °F |
Adequate ventilation is required when curing these products. Outgassing will occur above 300°F and cease after 750°F. An additional 30 minutes is required at the highest service temperature if service temperature is below 750°F. |
Aremco Corr-Paint™ CP4080 High Temperature Protective Coating Silicone, Aluminum Filled This silicone-based, heat resistant coatings are formulated using a state-of-the-art, VOC-compliant, water-dispersible silicone resin. CP4000 adheres to metals, ceramics, refractories, and quartz, a.. |
|||
Cure Time | 60.0 min @Temperature 200 °C |
1.00 hour @Temperature 392 °F |
1 hr at 450°F, 15 min at 1300°F |
Aremco Lamp-Coat™ LC4040-SG High Temperature Coating, Silicone White reflective coating for use on mercury vapor lamps and other high temperature glass and quartz components to 1200 ºF (649 ºC). |
|||
Cure Time | 60.0 min @Temperature 152 °C |
1.00 hour @Temperature 305 °F |
|
TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 78A MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is c.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N990 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber, No Milling Time MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR N330 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 142 °C |
1.00 hour @Temperature 287 °F |
|
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N650 Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Cure Time | 60.0 min @Temperature 177 °C |
1.00 hour @Temperature 351 °F |
|
Henkel SynCore 9872.1 Syntactic Film Toughened, low density syntactic core, superior moisture resistance, co-curable with a wide variety of 350°F / 177°C curing epoxy prepregs. |