Polymer Property : Electrical Resistivity = 0.00000660 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000660 - 0.00000700 ohm-cm	0.00000660 - 0.00000700 ohm-cm
PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6 Heat Treatment Condition T6 (Quench in water at RT)abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of p..
Electrical Resistivity	0.00000660 - 0.0000101 ohm-cm	0.00000660 - 0.0000101 ohm-cm	17-26% IACS Conductivity
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM00 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Electrical Resistivity	0.00000660 - 0.0000101 ohm-cm	0.00000660 - 0.0000101 ohm-cm	17-26% IACS Conductivity
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM02 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 97%Stress Relaxation after 1000 hrs @ 200Â°C: 76%Formability Ratio, 90Â° Bend, R..
Electrical Resistivity	0.00000660 - 0.0000101 ohm-cm	0.00000660 - 0.0000101 ohm-cm	17-26% IACS Conductivity
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM04 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 98%Stress Relaxation after 1000 hrs @ 200Â°C: 77%Formability Ratio, 90Â° Bend, R..
Electrical Resistivity	0.00000660 - 0.0000101 ohm-cm	0.00000660 - 0.0000101 ohm-cm	17-26% IACS Conductivity
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM06 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 99%Stress Relaxation after 1000 hrs @ 200Â°C: 78%Formability Ratio, 90Â° Bend, R..
Electrical Resistivity	0.00000660 - 0.0000101 ohm-cm	0.00000660 - 0.0000101 ohm-cm	17-26% IACS Conductivity
Materion BrushformÂ® 290 Beryllium Copper Alloy Strip; TM08 Temper (UNS C17200) Treatment required for max strength: Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100Â°C: 99%Stress Relaxation after 1000 hrs @ 200Â°C: 78%Formability Ratio, 90Â° Bend, R..