| Haynes 188 alloy, 0% cold reduction, 3.2 mm thick sheet |
Superalloy |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet |
Superalloy |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet |
Superalloy |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 30% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet |
Superalloy |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1065°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, hot rolled and 1175°C solution annealed plate |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 0 hours at 870°C (1600°F) |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 1000 hours at 870°C (1600°F) |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 16000 hours at 870°C (1600°F) |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 4000 hours at 870°C (1600°F) |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 650°C (1200°F) |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 870°C (1600°F) |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 15% cold reduction, aged at 370°C (700°F) for 1 hour |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 20 % cold reduction |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 370°C (700°F) for 1 hour |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 20% cold reduction, aged at 595°C (1100°F) for 2 hours |
Superalloy |
|
| Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet |
Superalloy |
|
| Haynes NS-163® Cobalt Alloy |
Cobalt Alloy |
|
| Haynes Ultimet® alloy, 1.6 mm sheet |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, 12.7-50.8 mm bar |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, 6.3-38.1 mm plate |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 316°C |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, aged 1000 hours at 982°C |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, all-weld metal, GTAW weld |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, all-weld metal, SMAW weld |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, mill annealed |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, plate, GMAW weld (short) |
Superalloy |
Ultimet®
|
| Haynes Ultimet® alloy, plate, GMAW weld (spray) |
Superalloy |
Ultimet®
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet |
Superalloy |
|
| Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes |
Superalloy |
|
| Haynes 188 alloy, cold rolled and 1175°C solution annealed sheet |
Superalloy |
|
| Haynes 188 alloy, plate at RT after 8000 hours at 760°C (1400°F) |
Superalloy |
|
| Haynes 25 alloy, cold rolled and 1205°C (2200°F) solution annealed sheet |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 10% cold reduction |
Superalloy |
|
| Haynes 25 alloy, cold worked sheet, 15 % cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1175°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 25% cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1065°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1120°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 25% cold reduction, 1175°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 760°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 100 hours of 870°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 650°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 1000 hours of 870°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 2500 hours of 650°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 650°C exposure |
Superalloy |
|
| Haynes 25 alloy, room temperature sheet after 500 hours of 870°C exposure |
Superalloy |
|
| Haynes 25 alloy, sheet |
Superalloy |
|
| Haynes 25 alloy, vacuum investment castings, solution treated |
Superalloy |
|
| Haynes 25 alloy, room temperature after 0% cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 10% cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1065°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1175°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 15% cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1120°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 20% cold reduction |
Superalloy |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes |
Superalloy |
|
| Haynes 25 alloy, room temperature after 15% cold reduction, 1065°C anneal for 5 minutes |
Superalloy |
|