3M Dyneon™ FC 2161X Fluoroelastomer  (discontinued **)

Category Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ FC 2161X Fluoroelastomer  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Composition: di-polymer of vinylidene fluoride and hexafluoropropyleneMedium viscosityProcess targets: compression and transfer molding, and calenderingProprietary incorporated cure technologyExcellent demolding of complex geometric profilesInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Specific Gravity 1.80 g/cc
1.80 g/cc
Mooney Viscosity 62

@Temperature 121 °C
62

@Temperature 250 °F
ML1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 73
73
Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break 12.1 MPa
1750 psi
Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break 370 %
370 %
Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D4645
100% Modulus 0.00248 GPa
0.360 ksi
Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Thermal Properties Metric English Comments
Transformation Temperature -18.0 °C
-0.400 °F
TR10; ASTM D1329
Component Elements Properties Metric English Comments
Fluorine, F 65.9 %
65.9 %
Descriptive Properties Value Comments
5`50, Time to 50% cure, minutes 0.9
177°C
Color Opaque Off-White
MH, Maximum Torque, inch-lb @ 177°C 8
ML, Minimum Torque inch-lb @ 177°C 2.2
Solubility Ketones and Esters
t`90 - Time to 90% cure @ 177°C - minutes 1.1
ts2 - Time to 2 in-lb rise from min @ 177°C - min 0.8