3M Dyneon™ FE 5730 Fluoroelastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE)
Manufacturer 3M Dyneon™
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ FE 5730 Fluoroelastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Composition: Ter-polymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethyleneLower fluorine version of FE 5830QProcess targets: extrusion onlyProprietary incorporated cure technologyProduces smooth extrudates without the use of processing aidesCan be formulated to meet -40°C mandrel bend fuel hose specificationsCan be formulated to yield good permeation resistance to automotive fuelsInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Specific Gravity 1.87 g/cc
1.87 g/cc
Mooney Viscosity 36

@Temperature 121 °C
36

@Temperature 250 °F
ML1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 71
71
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break 10.1 MPa
1460 psi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break 330 %
330 %
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
100% Modulus 0.00259 GPa
0.375 ksi
Press Cure 7 minutes @ 177°C, Post Cure 24 hours @ 260°C
Compression Set 45 %
45 %
Aged 70 hours @ 200°C
Thermal Properties Metric English Comments
Transformation Temperature -12.0 °C
10.4 °F
TR10; ASTM D1329
Component Elements Properties Metric English Comments
Fluorine, F 69.2 %
69.2 %
Descriptive Properties Value Comments
Color Opaque Off-White
MH, Maximum Torque 9.2 inch-lb
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ML, Minimum Torque 1.1 inch-lb
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
Solubility Ketones and Esters
t`50, Time to 50% cure 1.4 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t`90 - Time to 90% cure 1.9 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ts2 - Time to 2 in-lb rise from min 1.3 minutes
100 cpm, 0.5° Arc, 6 Minutes @ 177°C