3M Dyneon™ PFE 132TBZ High Temperature Perfluoroelastomer

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer
Manufacturer 3M
Trade Name Dyneon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ PFE 132TBZ High Temperature Perfluoroelastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Dyneon™ PFE 132TBZ is a technically advanced high temperature perfluorelastomer (HT PFE). It is designed to meet the challenges of higher temperature plasma applications. It is classified as FFKM per ASTM D1418. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability.Features and Benefits:Upper use temperature of 315°CExcellent compression set resistance offering enhanced sealing force retention and seal lifeIdeal for dry side (thermal processes) semiconductor applications including plasmaLow metal ion content with low extractablesInformation provided by 3M
Physical Properties Metric English Comments
Density 2.00 g/cc
0.0723 lb/in³
Mooney Viscosity 110

@Temperature 121 °C
110

@Temperature 250 °F
ML (1+10)
Mechanical Properties Metric English Comments
Hardness, Shore A 79
79
Press Cure 15 Minutes @ 188°C (370°F), Post Cure 24 Hours @ 250°C (482°F); ASTM D2240
Tensile Strength at Break 15.6 MPa
2260 psi
Press Cure 15 Minutes @ 188°C (370°F), Post Cure 24 Hours @ 250°C (482°F)
Elongation at Break 241 %
241 %
Press Cure 15 Minutes @ 188°C (370°F), Post Cure 24 Hours @ 250°C (482°F)
100% Modulus 0.00690 GPa
1.00 ksi
Press Cure 15 Minutes @ 188°C (370°F), Post Cure 24 Hours @ 250°C (482°F)
Compression Set 36 %

@Temperature 232 °C,
Time 252000 sec
36 %

@Temperature 450 °F,
Time 70.0 hour
-214 O-rings, 25% Deformation; ASTM D395 Method B
73 %

@Temperature 300 °C,
Time 252000 sec
73 %

@Temperature 572 °F,
Time 70.0 hour
-214 O-rings, 25% Deformation; ASTM D395 Method B
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 315 °C
599 °F
Brittleness Temperature -35.0 °C
-31.0 °F
Transformation Temperature -2.00 °C
28.4 °F
TR 10
Descriptive Properties Value Comments
Color White
Form Crumb
MH, Maximum Torque 16.0 In-lb
100 cpm, 0.5° Arc, 12 Minutes @ 188°C (370°F), ASTM D5289
ML, Minimum Torque 1.3 In-lb
100 cpm, 0.5° Arc, 12 Minutes @ 188°C (370°F), ASTM D5289
t’50, Time to 50% Cure 2.8 minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C (370°F), ASTM D5289
t’90, Time to 90% Cure 6.2 minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C (370°F), ASTM D5289
ts2, Time to 2 Inch-lb Rise from Minimum 1.7 minutes
100 cpm, 0.5° Arc, 12 Minutes @ 188°C (370°F), ASTM D5289