Material Notes:
3M™ Dyneon™ PVDF 11010/0000 is a copolymer of VF2 and HFP (hexafluoropropylene). Recommended for flared tubing, it combines excellent chemical resistance, and dimensional stability with a moderate degree of flexibility. PVDF is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, food processing, and pharmaceutical equipment and battery applications.Good flexibility and mechanical strength in extruded tubingFlareability of extruded tubingGood chemical resistance to acids, bases, alcohols, ectMeets requirements of Factory Mutual Standard FM 4910NSF 61 CertificationInformation provided by Dyneon, A 3M Company
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
ISO 1183
Water Absorption <= 0.040 %
<= 0.040 %
24 hr @ 23°C; ISO 62 (method 1)
Melt Index of Compound 2.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
6.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
50mm/min; ASTM D638
Tensile Strength, Yield 27.0 MPa
3920 psi
50mm/min; ASTM D638
Elongation at Break 400 %
400 %
50mm/min; ASTM D638
Flexural Strength 37.0 MPa
5370 psi
2mm/min; ASTM D790
Flexural Modulus 0.900 GPa
131 ksi
2mm/min; ASTM D790
Thermal Properties Metric English Comments
Melting Point 160 °C
320 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 52.0 °C
126 °F
Vicat Softening Point 150 °C
302 °F
1 kg load; ISO 306
Flammability, UL94 V-0
V-0
Oxygen Index >= 44 %

@Thickness 3.00 mm
>= 44 %

@Thickness 0.118 in
Sheet; ASTM D2863
Descriptive Properties Value Comments
Form Granules