3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Weld Epoxy Adhesive EC-2216 B/A in chemical composition. Scotch-Weld epoxy adhesive 2216 B/A may be used for aircraft and aerospace applications if proper Certificates of Test have been issued an issued and material meets all aircraft manufacturer’s specification requirements.Information provided by 3M
Physical Properties Metric English Comments
Brookfield Viscosity 75000 - 150000 cP
75000 - 150000 cP
Base, RVF #7 spindle, 20 rpm
550000 - 900000 cP
550000 - 900000 cP
Accelerator, RVF #7 spindle, 20 rpm
Mechanical Properties Metric English Comments
Hardness, Shore D 65 - 70
65 - 70
Shear Modulus 0.342 GPa

@Temperature 24.0 °C
49.6 ksi

@Temperature 75.2 °F
Torsion Pendulum Method
1.509 GPa

@Temperature 0.000 °C
218.8 ksi

@Temperature 32.0 °F
Torsion Pendulum Method
1.946 GPa

@Temperature -40.0 °C
282.3 ksi

@Temperature -40.0 °F
Torsion Pendulum Method
2.1984 GPa

@Temperature -60.0 °C
318.85 ksi

@Temperature -76.0 °F
Torsion Pendulum Method
2.74 GPa

@Temperature -100 °C
398 ksi

@Temperature -148 °F
Torsion Pendulum Method
Shear Strength 4.21 MPa
610 psi
Overlap, Polyphenylene Oxide/PPO; ASTM D1002
7.65 MPa
1110 psi
Overlap, Acrylic/Acrylic; ASTM D1002
7.86 MPa
1140 psi
Overlap, ABS/ABS Plastic; ASTM D1002
8.89 MPa
1290 psi
Overlap, PC/ABS Alloy / PC/ABS Alloy; ASTM D1002
11.4 MPa
1650 psi
Overlap, Fiber Reinforced Polyester/Reinforced Polyester; ASTM D1002
11.9 MPa
1730 psi
Overlap, Polycarbonate/Polycarbonate; ASTM D1002
16.2 MPa
2350 psi
Overlap, Al/Al; ASTM D1002
18.3 MPa
2650 psi
Overlap, Etched Al, 100% RH at 49°C for 30 days
18.6 MPa
2700 psi
Overlap, Etched Al, Tap water at RT for 30 days
19.0 MPa
2750 psi
Overlap, Etched Al, JP-4 for 30 days
21.0 MPa
3050 psi
Overlap, Etched Al, Anti-icing Fluid at RT for 7 days
21.4 MPa
3100 psi
Overlap, Etched Al, Hydrocarbon Fluid for 7 days
21.4 MPa
3100 psi
Overlap, CRS/CRS; ASTM D1002
22.4 MPa
3250 psi
Overlap, Etched Al, Tap water at RT for 14 days
22.8 MPa
3300 psi
Overlap, Etched Al, Salt Spray at RT for 30 days
23.4 MPa
3400 psi
Overlap, Etched Al, 100% RH at 49°C for 14 days
24.1 MPa
3500 psi
Overlap, Etched Al, Hydraulic Oil at RT for 30 days
26.9 MPa
3900 psi
Overlap, Etched Al, Salt Spray at RT for 14 days
30.51 MPa
4425 psi
Overlap, Etched Al, Air at 71°C for 35 days
30.7 MPa
4450 psi
Overlap, Etched Al, Air at 149°C for 40 days
2.76 MPa

@Temperature 82.0 °C
400 psi

@Temperature 180 °F
Overlap, Etched Aluminum; ASTM D1002
13.8 MPa

@Temperature -53.0 °C
2000 psi

@Temperature -63.4 °F
Overlap, Etched Aluminum; ASTM D1002
17.2 MPa

@Temperature 24.0 °C
2500 psi

@Temperature 75.2 °F
Overlap, Etched Aluminum; ASTM D1002
Peel Strength 4.38 kN/m
25.0 pli
T-Peel
Processing Properties Metric English Comments
Cure Time 480 - 720 min
8.00 - 12.0 hour
Time to Handling Strength
Descriptive Properties Value Comments
Appearance Tan
Accelerator
Tan
White
Base