3M Scotch-Weld™ DP190 Gray Epoxy Adhesive

Category Polymer , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ DP190 Gray Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Epoxy Adhesive DP190 Gray is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Gray and exhibits good peel, shear and environmental aging properties.Information provided by 3M
Physical Properties Metric English Comments
Brookfield Viscosity 40000 - 80000 cP
40000 - 80000 cP
Accelerator, RFV #7 at 20 rpm
75000 - 150000 cP
75000 - 150000 cP
Base, RFV #7 at 20 rpm
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
ASTM D2240
Tensile Strength at Break 24.1 MPa
3500 psi
ASTM D882
Elongation at Break 30 %
30 %
ASTM D882
Shear Strength 0.345 MPa
50.0 psi
Overlap, Polypropylene
2.07 MPa
300 psi
Overlap, Glass, Borosilicate
2.07 MPa
300 psi
Overlap, Glass, +3M Scotch-Weld Primer 3901
3.45 MPa
500 psi
Overlap, Acrylic
4.83 MPa
700 psi
Overlap, ABS
5.52 MPa
800 psi
Overlap, Polycarbonate
5.52 MPa
800 psi
Overlap, PVC
7.58 MPa
1100 psi
Overlap, Wood, Fir
9.65 MPa
1400 psi
Overlap, CRS
10.3 MPa
1500 psi
Overlap, Sanded Aluminum
11.0 MPa
1600 psi
Overlap, Fiberglass
17.2 MPa
2500 psi
Overlap, Etched Aluminum
2.76 MPa

@Temperature 82.0 °C
400 psi

@Temperature 180 °F
Overlap
4.14 MPa

@Temperature 66.0 °C
600 psi

@Temperature 151 °F
Overlap
6.89 MPa

@Temperature 49.0 °C
1000 psi

@Temperature 120 °F
Overlap
10.3 MPa

@Temperature -55.0 °C
1500 psi

@Temperature -67.0 °F
Overlap
17.2 MPa

@Temperature 21.0 °C
2500 psi

@Temperature 69.8 °F
Overlap
Peel Strength 0.351 kN/m

@Temperature 82.0 °C
2.00 pli

@Temperature 180 °F
180°
0.526 kN/m

@Temperature -55.0 °C
3.00 pli

@Temperature -67.0 °F
180°
0.701 kN/m

@Temperature 66.0 °C
4.00 pli

@Temperature 151 °F
180°
1.75 kN/m

@Temperature 49.0 °C
10.0 pli

@Temperature 120 °F
180°
3.51 kN/m

@Temperature 21.0 °C
20.0 pli

@Temperature 69.8 °F
180°
Thermal Properties Metric English Comments
CTE, linear 62.0 µm/m-°C

@Temperature 5.00 - 25.0 °C
34.4 µin/in-°F

@Temperature 41.0 - 77.0 °F
Below Tg
177 µm/m-°C

@Temperature 65.0 - 140 °C
98.3 µin/in-°F

@Temperature 149 - 284 °F
Above Tg
Thermal Conductivity 0.381 W/m-K

@Thickness 6.35 mm,
Temperature 43.3 °C
2.64 BTU-in/hr-ft²-°F

@Thickness 0.250 in,
Temperature 110 °F
Glass Transition Temp, Tg 7.00 °C
44.6 °F
Onset
20.0 °C
68.0 °F
Mid-Point
Electrical Properties Metric English Comments
Volume Resistivity 5.00e+12 ohm-cm
5.00e+12 ohm-cm
ASTM D257
Dielectric Constant 6.5

@Frequency 1000 Hz
6.5

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 32.7 kV/mm

@Thickness 0.762 mm
830 kV/in

@Thickness 0.0300 in
ASTM D149
Dissipation Factor 0.090

@Frequency 1000 Hz
0.090

@Frequency 1000 Hz
ASTM D150
Processing Properties Metric English Comments
Cure Time 360 min
6.00 hour
Tack-free time
480 - 720 min
8.00 - 12.0 hour
Time to Handling Strength
10100 min
168 hour
Full Cure
Descriptive Properties Value Comments
Appearance Gray
Accelerator
Gray
White
Base