3M Scotch-Weld™ EC-2086 Structural Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ EC-2086 Structural Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Structural Adhesive EC-2086 is a one-part, 100% solids thermosetting liquid adhesives.Information provided by 3M

Mechanical Properties	Metric	English	Comments
Shear Strength	18.16 MPa	2634 psi	Etched Aluminum Overlap, Salt Spray @ 35°C for 356 days
	19.7 MPa	2850 psi	Etched Aluminum Overlap, 100% RH @ 49°C for 356 days
	22.95 MPa	3328 psi	Etched Aluminum Overlap, 100% RH @ 49°C for 180 days
	25.3 MPa	3670 psi	Etched Aluminum Overlap, 100% RH @ 49°C for 90 days
	28.5 MPa	4140 psi	Etched Aluminum Overlap Freon 22 Resistance, 60 days @ RT
	29.13 MPa	4225 psi	Etched Aluminum Overlap Freon 22 Resistance, 1 year @ RT
	30.8 MPa	4470 psi	Etched Aluminum Overlap Freon 22 Resistance, 30 days @ RT
	32.1 MPa	4650 psi	Etched Aluminum Overlap Freon 22 Resistance, Control
	32.35 MPa	4692 psi	Etched Aluminum Overlap, Salt Spray @ 35°C for 180 days
	32.5 MPa	4720 psi	Etched Aluminum Overlap, 100% RH @ 49°C
	33.3 MPa	4830 psi	Etched Aluminum Overlap, Salt Spray @ 35°C for 90 days
	34.92 MPa	5064 psi	Etched Aluminum Overlap, Salt Spray @ 35°C
	39.4 MPa	5710 psi	Etched Aluminum Overlap, Hydraulic Oil @ RT
	39.88 MPa	5784 psi	Etched Aluminum Overlap, Tap Water @ RT
	41.11 MPa	5962 psi	Etched Aluminum Overlap, Tap Water @ RT for 90 days
	41.53 MPa	6024 psi	Etched Aluminum Overlap, White Gas @ RT
	42.1 MPa	6100 psi	Etched Aluminum Overlap, Tap Water @ RT for 356 days
	42.42 MPa	6152 psi	Etched Aluminum Overlap, Tap Water @ RT for 180 days
	0.896 MPa @Temperature 177 °C	130 psi @Temperature 351 °F	Solvent Wiped Cold Rolled Steel Overlap
	3.31 MPa @Temperature 121 °C	480 psi @Temperature 250 °F	Solvent Wiped Cold Rolled Steel Overlap
	3.45 MPa @Temperature 177 °C	500 psi @Temperature 351 °F	Etched Aluminum Overlap
	15.2 MPa @Temperature 121 °C	2200 psi @Temperature 250 °F	Etched Aluminum Overlap
	16.3 MPa @Temperature 82.0 °C	2360 psi @Temperature 180 °F	Solvent Wiped Cold Rolled Steel Overlap
	18.6 MPa @Temperature 24.0 °C	2700 psi @Temperature 75.2 °F	Solvent Wiped Cold Rolled Steel Overlap
	20.7 MPa @Temperature -55.0 °C	3000 psi @Temperature -67.0 °F	Etched Aluminum Overlap
	23.0 MPa @Temperature -40.0 °C	3340 psi @Temperature -40.0 °F	Solvent Wiped Cold Rolled Steel Overlap
	24.1 MPa @Temperature 232 °C	3500 psi @Temperature 450 °F	Bond Line
	29.6 MPa @Temperature 218 °C	4300 psi @Temperature 424 °F	Bond Line
	34.5 MPa @Temperature 82.0 °C	5000 psi @Temperature 180 °F	Etched Aluminum Overlap
	34.5 MPa @Temperature 24.0 °C	5000 psi @Temperature 75.2 °F	Etched Aluminum Overlap
	36.5 MPa @Temperature 204 °C	5300 psi @Temperature 399 °F	Bond Line
	37.9 MPa @Temperature 11.0 °C	5500 psi @Temperature 51.8 °F	Bond Line
	37.9 MPa @Temperature 177 °C	5500 psi @Temperature 351 °F	Bond Line
Peel Strength	8.77 kN/m	50.0 pli	Solvent Wiped T-Peel

Thermal Properties	Metric	English	Comments
CTE, linear	47.0 µm/m-°C @Temperature -18.0 - 27.0 °C	26.1 µin/in-°F @Temperature -0.400 - 80.6 °F
Thermal Conductivity	0.429 W/m-K	2.98 BTU-in/hr-ft²-°F

Electrical Properties	Metric	English
Volume Resistivity	3.60e+14 ohm-cm	3.60e+14 ohm-cm
Surface Resistance	1.00e+17 ohm	1.00e+17 ohm
Dielectric Constant	10.8 @Temperature 23.0 °C	10.8 @Temperature 73.4 °F
	11.4 @Temperature 60.0 °C	11.4 @Temperature 140 °F
Dielectric Strength	4.84 kV/mm	123 kV/in
Dissipation Factor	0.016 @Temperature 23.0 °C	0.016 @Temperature 73.4 °F
	0.228 @Temperature 60.0 °C	0.228 @Temperature 140 °F
Arc Resistance	34 sec	34 sec

Descriptive Properties	Value	Comments
Appearance	Gray