3M Scotch-Weld™ EZ250120 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Scotch-Weld™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Scotch-Weld™ EZ250120 Polyurethane Reactive (PUR) Easy 250 Wood Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Scotch-Weld™ Polyurethane Reactive (PUR) Easy 250 Wood Adhesive is 100% solid, warm temperature applied, moisture curing urethanes. This product bonds well to wood and wood bases surfaces as well as select plastics. This product offers a wide variation of open and set times as well as the ability to produce very thin bond lines. Medium setting, low viscosity ideal for bonding wood and producing thin glue lines.Information provided by 3M
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
Brookfield Viscosity 3000 cP
3000 cP
Thermosel using spindle #27
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
Tensile Strength at Break 27.6 MPa
4000 psi
ASTM D638 Die C
Elongation at Break 625 %
625 %
ASTM D638 Die C
Shear Strength 4.27 MPa

@Temperature 82.0 °C
620 psi

@Temperature 180 °F
Overlap, Maple
13.4 MPa

@Temperature 23.0 °C
1950 psi

@Temperature 73.4 °F
Overlap, Maple
7.619 MPa

@Time Error in fixSigDigits: @digits must be between 1 a sec
1105 psi

@Time Error in fixSigDigits: @digits must be between 1 a hour
Overlap, Maple conditioned for 7 days AT RT/50% RH
12.45 MPa

@Time 3600 sec
1805 psi

@Time 1.00 hour
Overlap, Maple conditioned for 7 days AT RT/50% RH
13.20 MPa

@Time 86400 sec
1915 psi

@Time 24.0 hour
Overlap, Maple conditioned for 7 days AT RT/50% RH
13.4 MPa

@Time 605000 sec
1950 psi

@Time 168 hour
Overlap, Maple conditioned for 7 days AT RT/50% RH
13.62 MPa

@Time 259000 sec
1975 psi

@Time 72.0 hour
Overlap, Maple conditioned for 7 days AT RT/50% RH
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Processing Properties Metric English Comments
Cure Time 2.00 min
0.0333 hour
Set Time
Descriptive Properties Value Comments
Appearance white/off-white