3M Scotch-Weld™ TE031 Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE031 Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade with fast set time ideal for bonding a wide variety of plastics including polystyrene and polyacrylic.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	>= 1.04 g/cc	>= 0.0376 lb/in³
Brookfield Viscosity	13000 cP	13000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	50	50
Tensile Strength at Break	26.9 MPa	3900 psi	ASTM D638 Die C
Elongation at Break	725 %	725 %	ASTM D638 Die C
Tensile Modulus	0.0386 GPa	5.60 ksi	ASMT D638 Die C
Shear Strength	2.34 MPa @Temperature 82.0 °C	340 psi @Temperature 180 °F	Overlap, Maple
	4.90 MPa @Temperature 23.0 °C	710 psi @Temperature 73.4 °F	Overlap, Polystyrene, Substrate Failure
	5.52 MPa @Temperature 82.0 °C	800 psi @Temperature 180 °F	Overlap, FRP
	9.17 MPa @Temperature 23.0 °C	1330 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	9.31 MPa @Temperature 23.0 °C	1350 psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	10.6 MPa @Temperature 23.0 °C	1540 psi @Temperature 73.4 °F	Overlap, Maple
	11.5 MPa @Temperature 23.0 °C	1670 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	13.0 MPa @Temperature 23.0 °C	1890 psi @Temperature 73.4 °F	Overlap, FRP
	14.5 MPa @Temperature 23.0 °C	2100 psi @Temperature 73.4 °F	Overlap, Polycarbonate
Peel Strength	0.526 kN/m	3.00 pli	180°, Aluminum
	0.526 kN/m	3.00 pli	180°, Glass
	2.80 kN/m	16.0 pli	T-Peel, Initial, Substrate failure
	3.86 kN/m	22.0 pli	T-Peel, Aged 71°C for 2 weeks, Substrate failure
	11.4 kN/m	65.0 pli	180°, Polystyrene, Cotton duck failed during testing
	13.5 kN/m	77.0 pli	180°, Polyacrylic, Cotton duck failed during testing
	14.7 kN/m	84.0 pli	180°, ABS, Cotton duck failed during testing
	16.7 kN/m	95.0 pli	180°, Polycarbonate, Cotton duck failed during testing
	16.8 kN/m	96.0 pli	180°, FRP, Cotton duck failed during testing
	17.5 kN/m	100 pli	180°, PVC, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	0.500 min	0.00833 hour	Set Time