3M Weatherban™ 5354 Sealant Tape

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Weatherban™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Weatherban™ 5354 Sealant Tape.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Weatherban™ Sealant Tape 5354 is a high tack extruded synthetic rubber, non-curing sealant in tape form.It can be used to seal between glass, metal, wood and many plastics.Easy to compress and has exceptional cold flow resistance.Good adhesion to dry surfaces and will stay in place when positioned vertically, overhead or around sharp corners.Low moisture vapor transmission.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	1.41 g/cc	0.0509 lb/in³
Solids Content	100 %	100 %
Water Vapor Transmission	0.390 g/m²/day	0.0251 g/100 in²/day	ASTM E96-66

Mechanical Properties	Metric	English	Comments
Hardness, Shore OO	60	60
	62 @Temperature 110 °C, Time 605000 sec	62 @Temperature 230 °F, Time 168 hour	Heat Aging
Shear Strength	0.0483 MPa @Temperature 110 °C, Time 605000 sec	7.00 psi @Temperature 230 °F, Time 168 hour	Overlap
	0.0717 MPa @Temperature 110 °C, Time 605000 sec	10.4 psi @Temperature 230 °F, Time 168 hour	Overlap
	0.0752 MPa @Temperature 110 °C, Time 605000 sec	10.9 psi @Temperature 230 °F, Time 168 hour	Overlap
	0.0820 MPa @Temperature 110 °C, Time 605000 sec	11.9 psi @Temperature 230 °F, Time 168 hour	Overlap
	0.0896 MPa @Temperature 110 °C, Time 605000 sec	13.0 psi @Temperature 230 °F, Time 168 hour	Overlap
	0.0483 MPa @Time 86400 sec	7.00 psi @Time 24.0 hour	Overlap
	0.0689 MPa @Time 86400 sec	10.0 psi @Time 24.0 hour	Overlap
	0.0689 MPa @Time 86400 sec	10.0 psi @Time 24.0 hour	Overlap
	0.0724 MPa @Time 86400 sec	10.5 psi @Time 24.0 hour	Overlap
	0.0724 MPa @Time 86400 sec	10.5 psi @Time 24.0 hour	Overlap

Processing Properties	Metric	English	Comments
Shelf Life	15.0 Month	15.0 Month

Descriptive Properties	Value	Comments
Color	Black