3M Z100™ Restorative Dental Composite

Category Polymer , Thermoset , Methacrylate
Manufacturer 3M
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Z100™ Restorative Dental Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Z100™ restorative is an all purpose, esthetic, light cured dental composite. 3M Restorative Z100 features a translucency and opalescence similar to that of natural teeth and is used for porcelain repair and metal masking. Bonding to tooth structure is accomplished by using a dental adhesive system, such as 3M™ Single Bond or 3M™ Scotchbond Multi-Purpose Adhesive Systems. The restorative is available in a variety of shades and is packaged in syringes or capsules.The matrix of this composite is a resin consisting of BIS-GMA (Bisphenol A diglycidyl ether dimethacrylate) and TEGDMA (tri{ethylene glycol] dimethacrylate). This light-cured resin is filled with 66% (volume) silica/zirconia. The filler average particle size is 0.6 µm.Filtek P60 exhibits higher volumetric shrinkage upon curing than 3M™ Filtek™ P60 or Filtek™ Z250. An example from the manufacturer shows shrinkage of 2.4% after 5 minutes and 2.6% after 30 minutes; sample geometry will effect actual values. Wet fracture toughness is 1.3 MN/m. The wear rate in an in-vitro 3-body wear test gives 2.2 µLoss/39,000 cycles. Compared to other dental composites, it has a medium-high diametral tensile strength, medium-high compressive strength, high compressive modulus, medium-high flexural strength and a high flexural modulus.Information provided by 3M. Contact 3M for further information before specifying or using this product.
Physical Properties Metric English Comments
Viscosity 3.00e+6 cP
3.00e+6 cP
target viscosity before cure
Mechanical Properties Metric English Comments
Hardness, Barcol 71
71
Bottom of sample; cure light intensity of 660 mWatts/cm². C2 shade.
85
85
Top of sample; cure light intensity of 660 mWatts/cm². C2 shade.
Tensile Strength, Ultimate 105 MPa
15200 psi
Diametral tensile strength
Flexural Yield Strength 135 MPa
19600 psi
Flexural Modulus 14.5 GPa
2100 ksi
Compressive Yield Strength 470 MPa
68200 psi
Adhesive Bond Strength 28.0 MPa
4060 psi
Bond strength to dentin using a dental adhesive system; C2 color
Processing Properties Metric English Comments
Processing Temperature 20.0 °C
68.0 °F
Light cured