A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon

Category Polymer , Thermoplastic , Nylon
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ASTM D792
Linear Mold Shrinkage 0.0020 cm/cm

@Thickness 3.175 mm
0.0020 in/in

@Thickness 0.1250 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 133 MPa
19300 psi
ASTM D638
Flexural Strength 219 MPa
31800 psi
ASTM D790
Flexural Modulus 8.763 GPa
1271 ksi
ASTM D790
Izod Impact, Notched 0.694 J/cm
1.30 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.17 J/cm
15.3 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 243 °C
469 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 223 °C
433 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying