A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Voloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 97.0 MPa | 14100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 156 MPa | 22600 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.35 J/cm | 4.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 271 - 285 °C | 520 - 545 °F |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105/GF/30/TF/15 PEEK, with glass fiber and PTFE
- SABIC Innovative Plastics LNP STAT-KON DD000CEX PC
- SABIC Innovative Plastics Xenoy® 1731J PBT+PC (Asia Pacific)
- Star Plastics ABSLG3030 Molding Grade ABS, Low Gloss
- Total 1285 HDPE film
- Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade
- Dow Corning Q7-2587 30% SIMETHICONE EMULSION USP
- Covestro Makrolon® DP1-1888* Polycarbonate, 20% Glass Filled
- Abatron AboCast 8110-8/AboCure 8110-1 Flexible Epoxy
- Asahi Kasei Thermofil P-20CC-0734A 20% Calcium Carbonate Reinforced
Copyright © lookpolymers.com All Rights Reserved