A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionFormion® FI 120E is a non-reinforced, transparent, extrusion grade Zinc Ionomer. It has been formulate for high durability, cut and puncture resistance, and low temperature ductility.ApplicationFormion® FI 120E is targeted for exterior or interior appearance or packaging applications in film, blow molding, thermoforming or extrusion applications, which may require high or low gloss, excellent colorability or transparency. Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 0.960 g/cc
0.960 g/cc
ISO 1183/1
Linear Mold Shrinkage 0.0060 - 0.018 cm/cm

@Thickness 3.20 mm,
Time 259000 sec
0.0060 - 0.018 in/in

@Thickness 0.126 in,
Time 72.0 hour
ISO 294
Mechanical Properties Metric English Comments
Hardness, Shore D 63
63
15 sec delay; ISO 868
Tensile Strength, Ultimate 21.0 MPa
3050 psi
at max load; ISO 527
Elongation at Break 225 %
225 %
ISO 527
Flexural Modulus 0.227 GPa
32.9 ksi
Tangent; ISO 178
Izod Impact, Notched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
Melting Point 105 °C
221 °F
10°C per minute; ISO 3146
Deflection Temperature at 0.46 MPa (66 psi) 39.0 °C

@Thickness 3.17 mm
102 °F

@Thickness 0.125 in
ISO 75
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified