A. Schulman FORMION™ FI 393 Ionomer

Category Polymer , Thermoplastic , Ionomer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman FORMION™ FI 393 Ionomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized to exceed SAE J1960 2500 kj/m2 automotive performance criteria, and is targeted for non painted, mold-in-color, exterior or interior appearance applications.Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.01 g/cc
1.01 g/cc
ISO 1183/1
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0050 in/in

@Thickness 0.126 in
aged 48 hrs at 121°C; ISO 294
0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0060 in/in

@Thickness 0.126 in
72 hr; ISO 294
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
15 sec delay; ISO 868
Tensile Strength, Ultimate 22.0 MPa
3190 psi
at max load; ISO 527
Elongation at Break 215 %
215 %
ISO 527
Flexural Modulus 0.950 GPa
138 ksi
Tangent; ISO 178
Izod Impact, Notched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 64.0 °C

@Thickness 3.20 mm
147 °F

@Thickness 0.126 in
ISO 75