A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman POLYFLAM™ FPP 1007E Talc Filled Homopolymer Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DescriptionPolyfort® FPP 1007E is a 40% talc filled homopolymer compound for extrusion applications.Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 34.0 MPa
4930 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Strength 62.0 MPa
8990 psi
ASTM D790
Flexural Modulus 3.31 GPa
480 ksi
ASTM D790
Izod Impact, Notched 0.320 J/cm
0.599 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 80.0 °C
176 °F
ASTM D648
UL RTI, Electrical 120 °C

@Thickness 0.780 mm
248 °F

@Thickness 0.0307 in
UL 746
120 °C

@Thickness 1.57 mm
248 °F

@Thickness 0.0618 in
UL 746
120 °C

@Thickness 3.17 mm
248 °F

@Thickness 0.125 in
UL 746
UL RTI, Mechanical with Impact 115 °C

@Thickness 0.780 mm
239 °F

@Thickness 0.0307 in
UL 746
115 °C

@Thickness 1.57 mm
239 °F

@Thickness 0.0618 in
UL 746
115 °C

@Thickness 3.17 mm
239 °F

@Thickness 0.125 in
UL 746
UL RTI, Mechanical without Impact 115 °C

@Thickness 0.780 - 1.57 mm
239 °F

@Thickness 0.0307 - 0.0618 in
UL 746
120 °C

@Thickness 3.17 mm
248 °F

@Thickness 0.125 in
UL 746
Flammability, UL94 HB

@Thickness 0.780 mm
HB

@Thickness 0.0307 in
HB

@Thickness 1.57 mm
HB

@Thickness 0.0618 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in