A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min | 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | ASTM D648 |