A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | POLYPUR™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.011 - 0.016 cm/cm @Thickness 3.20 mm |
0.011 - 0.016 in/in @Thickness 0.126 in |
48 hr, at 121°C; ASTM D955 |
| 0.0090 - 0.014 cm/cm @Thickness 3.20 mm, Time 259000 sec |
0.0090 - 0.014 in/in @Thickness 0.126 in, Time 72.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 47 | 47 | 15 sec delay; ASTM D2240 |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | 2 in/min, at max load; ASTM D638 |
| 39.0 MPa | 5660 psi | 20 in/min, at max load; ASTM D412 | |
| Elongation at Break | 500 % | 500 % | 20 in/min; ASTM D412 |
| Flexural Modulus | 0.0690 GPa | 10.0 ksi | 1.3 mm/min; ASTM D790 |
| Compression Set | 30 % | 30 % | Method B, 22 h, 23°C; ASTM D395 |
| 35 % | 35 % | Method B, 22 h, 70°C; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 150 µm/m-°C @Temperature -30.0 - 30.0 °C |
83.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM E831 |