A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer A. Schulman, Inc.
Trade Name SCHULADUR®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by A. Schulman.
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D792
Linear Mold Shrinkage 0.0020 cm/cm

@Thickness 3.175 mm
0.0020 in/in

@Thickness 0.1250 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa
20300 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Strength 205 MPa
29700 psi
ASTM D790
Flexural Modulus 8.998 GPa
1305 ksi
ASTM D790
Izod Impact, Notched 0.641 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.41 J/cm
12.0 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 227 °C
441 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ASTM D648
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Drying Temperature 130 °C
266 °F
Dry Time 2 - 4 hour
2 - 4 hour
Predrying