- A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GF50H 50% Glass Fiber Reinforced, Heat Stabilized 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.175 mm |
0.0010 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 |
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 T 20 Polypropylene Copolymer, 20% Micronized Talc
- Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber (discontinued **)
- Covestro Makrolon® DP1-1243 Polycarbonate, Extrusion (discontinued **)
- Schott RG665 Long Pass Filter
- Solvay Chemicals DIGLYCEROL
- Teknor Apex Monprene® MP-2850M Thermoplastic Elastomer
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 60A
- A. Schulman POLYBATCH™ UVK-90 UV Stabilizer Concentrate Based In Polyethylene
- 3M 1183 EMI Shielding Tape
- SABIC Innovative Plastics Valox® V3900WX PBT+PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved