A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | VOLOY™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman VOLOY™ 461 Glass Reinforced, Flame Retardant PBT Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 3.175 mm |
0.0020 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17200 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 183 MPa | 26500 psi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.73 J/cm | 12.6 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 30.0 - 65.6 °C | 86.0 - 150 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- Omni Plastics OmniTuff™ HPP GRC30 Homopolymer Polypropylene Glass Reinforced
- Pyrotek I-28 Insulating Board
- Polykemi AB SCANMID 6 B33^ E F15 Nylon 6, Glass Fiber Reinforced, Modified
- Kinlead PT11 Adhesive Tape Grade BOPP Plain Film (thickness: 25 µm)
- H.C. Starck Grade C Titanium Carbonitride
- SABIC Innovative Plastics LNP LUBRICOMP RL008 PA 66 (Europe-Africa-Middle East)
- Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized
- Arlon R34572R005 0.005" (0.127 mm) Cured Silicone Rubber with Fiberglass Substrate
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.5 PHR Thanecure® ZM
Copyright © lookpolymers.com All Rights Reserved