AFE Technologies Cronite 37Ni/18Cr/Nb No. HR32

Category Metal , Superalloy , Iron Base
Manufacturer AFE TEchnologies; North American Cronite
Trade Name Cronite
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF AFE Technologies Cronite 37Ni/18Cr/Nb No. HR32.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AFE Technologies/North American Cronite, Inc.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 480 MPa
69600 psi
As Cast
Tensile Strength, Yield 250 MPa
36300 psi
As Cast
Elongation at Break 8.0 %
8.0 %
As Cast; 5.65 A<sup>0.5</sup>
Rupture Strength 3.40 MPa

@Temperature 1150 °C,
Time 3.60e+7 sec
 493 psi

@Temperature 2100 °F,
Time 10000 hour
 Stress Rupture
5.30 MPa

@Temperature 1100 °C,
Time 3.60e+7 sec
 769 psi

@Temperature 2010 °F,
Time 10000 hour
 Stress Rupture
8.00 MPa

@Temperature 1050 °C,
Time 3.60e+7 sec
 1160 psi

@Temperature 1920 °F,
Time 10000 hour
 Stress Rupture
12.0 MPa

@Temperature 1000 °C,
Time 3.60e+7 sec
 1740 psi

@Temperature 1830 °F,
Time 10000 hour
 Stress Rupture
18.0 MPa

@Temperature 950 °C,
Time 3.60e+7 sec
 2610 psi

@Temperature 1740 °F,
Time 10000 hour
 Stress Rupture
25.0 MPa

@Temperature 900 °C,
Time 3.60e+7 sec
 3630 psi

@Temperature 1650 °F,
Time 10000 hour
 Stress Rupture
34.0 MPa

@Temperature 850 °C,
Time 3.60e+7 sec
 4930 psi

@Temperature 1560 °F,
Time 10000 hour
 Stress Rupture
45.0 MPa

@Temperature 800 °C,
Time 3.60e+7 sec
 6530 psi

@Temperature 1470 °F,
Time 10000 hour
 Stress Rupture
59.0 MPa

@Temperature 750 °C,
Time 3.60e+7 sec
 8560 psi

@Temperature 1380 °F,
Time 10000 hour
 Stress Rupture
78.0 MPa

@Temperature 700 °C,
Time 3.60e+7 sec
 11300 psi

@Temperature 1290 °F,
Time 10000 hour
 Stress Rupture
Component Elements Properties Metric English Comments
Carbon, C 0.40 %
0.40 %
Chromium, Cr 18 %
18 %
Iron, Fe 40.6 %
40.6 %
As Remainder
Manganese, Mn 1.0 %
1.0 %
Nickel, Ni 37 %
37 %
Niobium, Nb (Columbium, Cb) 1.5 %
1.5 %
Silicon, Si 1.5 %
1.5 %