AK Steel TRAN-COR® H-0 CARLITE® DR® Grain Oriented Electrical Steel

Category Metal , Electronic/Magnetic Alloy , Ferrous Metal
Manufacturer AK Steel
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF AK Steel TRAN-COR® H-0 CARLITE® DR® Grain Oriented Electrical Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
TRAN-COR H CARLITE® high permeability electrical steels offer an outstanding degree of grain orientation, This combination of higher permeability with low residual stress offers the potential for lower core losses and less noisy transformer core structures, particularly at higher operating inductions, when compared to conventional grain oriented electrical steels. The core loss characteristics are further enhanced in the TRAN-COR H CARLITE DR® (Domain Refined) products where laser scribing is employed. In this process, a precisely focused laser beam is rapidly scanned across the steel surface. The micro-strain imparted into the material forces the pre-existing magnetic domains to subdivide. The finer domain structure reduces the distance that the domain walls must move during AC magnetization, thereby reducing eddy current losses. The result is far lower core loss than possible with conventional grain oriented electrical steels of comparable thickness. TRAN-COR H CARLITE products are suitable for all types of transformers while TRAN-COR H DR products are suitable for those types of transformers where a stress relief annealing treatment of the magnetic core is not used. Stress relief annealing will result in the eradication of the effect provided by the laser treatment and will result in a significant increase in core loss.Information provided by AK Steel.
Physical Properties Metric English Comments
Density 7.65 g/cc
0.276 lb/in³
Thickness 200 - 240 microns
7.87 - 9.45 mil
230 microns
9.06 mil
Nominal
Mechanical Properties Metric English Comments
Knoop Microhardness 173
173
Hardness, Rockwell B 83
83
Tensile Strength, Ultimate 359 MPa
52100 psi
In rolling direction
Tensile Strength, Yield 345 MPa
50000 psi
In rolling direction
Elongation at Break 11 %
11 %
In 2", rolling direction
Modulus of Elasticity 113.8 GPa
16510 ksi
In rolling direction
138 GPa
20000 ksi
At 20° to rolling direction
203 GPa
29400 ksi
At 90° to rolling direction
241 GPa
35000 ksi
At 45° to rolling direction
276 GPa
40000 ksi
At 55° to rolling direction
Electrical Properties Metric English Comments
Exciting Power (RMS) 0.00165 RMS AT/cm

@Magnetic Field 0.100 T,
Frequency 50.0 Hz
0.00260 RMS VA/lb

@Magnetic Field 0.100 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.00209 RMS AT/cm

@Magnetic Field 0.100 T,
Frequency 60.0 Hz
0.00330 RMS VA/lb

@Magnetic Field 0.100 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.00576 RMS AT/cm

@Magnetic Field 0.200 T,
Frequency 50.0 Hz
0.00910 RMS VA/lb

@Magnetic Field 0.200 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.00721 RMS AT/cm

@Magnetic Field 0.200 T,
Frequency 60.0 Hz
0.0114 RMS VA/lb

@Magnetic Field 0.200 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0120 RMS AT/cm

@Magnetic Field 0.300 T,
Frequency 50.0 Hz
0.0190 RMS VA/lb

@Magnetic Field 0.300 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0151 RMS AT/cm

@Magnetic Field 0.300 T,
Frequency 60.0 Hz
0.0238 RMS VA/lb

@Magnetic Field 0.300 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0199 RMS AT/cm

@Magnetic Field 0.400 T,
Frequency 50.0 Hz
0.0315 RMS VA/lb

@Magnetic Field 0.400 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0251 RMS AT/cm

@Magnetic Field 0.400 T,
Frequency 60.0 Hz
0.0397 RMS VA/lb

@Magnetic Field 0.400 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0294 RMS AT/cm

@Magnetic Field 0.500 T,
Frequency 50.0 Hz
0.0465 RMS VA/lb

@Magnetic Field 0.500 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0372 RMS AT/cm

@Magnetic Field 0.500 T,
Frequency 60.0 Hz
0.0588 RMS VA/lb

@Magnetic Field 0.500 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0403 RMS AT/cm

@Magnetic Field 0.600 T,
Frequency 50.0 Hz
0.0637 RMS VA/lb

@Magnetic Field 0.600 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0511 RMS AT/cm

@Magnetic Field 0.600 T,
Frequency 60.0 Hz
0.0807 RMS VA/lb

@Magnetic Field 0.600 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0528 RMS AT/cm

@Magnetic Field 0.700 T,
Frequency 50.0 Hz
0.0834 RMS VA/lb

@Magnetic Field 0.700 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.06675 RMS AT/cm

@Magnetic Field 0.800 T,
Frequency 50.0 Hz
0.1055 RMS VA/lb

@Magnetic Field 0.800 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.06700 RMS AT/cm

@Magnetic Field 0.700 T,
Frequency 60.0 Hz
0.1059 RMS VA/lb

@Magnetic Field 0.700 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.08282 RMS AT/cm

@Magnetic Field 0.900 T,
Frequency 50.0 Hz
0.1309 RMS VA/lb

@Magnetic Field 0.900 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.08485 RMS AT/cm

@Magnetic Field 0.800 T,
Frequency 60.0 Hz
0.1341 RMS VA/lb

@Magnetic Field 0.800 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.1018 RMS AT/cm

@Magnetic Field 1.00 T,
Frequency 50.0 Hz
0.1609 RMS VA/lb

@Magnetic Field 1.00 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.1055 RMS AT/cm

@Magnetic Field 0.900 T,
Frequency 60.0 Hz
0.1668 RMS VA/lb

@Magnetic Field 0.900 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.1245 RMS AT/cm

@Magnetic Field 1.10 T,
Frequency 50.0 Hz
0.1968 RMS VA/lb

@Magnetic Field 1.10 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.1294 RMS AT/cm

@Magnetic Field 1.00 T,
Frequency 60.0 Hz
0.2045 RMS VA/lb

@Magnetic Field 1.00 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.1522 RMS AT/cm

@Magnetic Field 1.20 T,
Frequency 50.0 Hz
0.2405 RMS VA/lb

@Magnetic Field 1.20 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.1585 RMS AT/cm

@Magnetic Field 1.10 T,
Frequency 60.0 Hz
0.2505 RMS VA/lb

@Magnetic Field 1.10 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.1863 RMS AT/cm

@Magnetic Field 1.30 T,
Frequency 50.0 Hz
0.2945 RMS VA/lb

@Magnetic Field 1.30 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.193 RMS AT/cm

@Magnetic Field 1.20 T,
Frequency 60.0 Hz
0.305 RMS VA/lb

@Magnetic Field 1.20 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.2287 RMS AT/cm

@Magnetic Field 1.40 T,
Frequency 50.0 Hz
0.3614 RMS VA/lb

@Magnetic Field 1.40 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.2356 RMS AT/cm

@Magnetic Field 1.30 T,
Frequency 60.0 Hz
0.3723 RMS VA/lb

@Magnetic Field 1.30 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.2819 RMS AT/cm

@Magnetic Field 1.50 T,
Frequency 50.0 Hz
0.4455 RMS VA/lb

@Magnetic Field 1.50 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.2876 RMS AT/cm

@Magnetic Field 1.40 T,
Frequency 60.0 Hz
0.4545 RMS VA/lb

@Magnetic Field 1.40 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.3523 RMS AT/cm

@Magnetic Field 1.50 T,
Frequency 60.0 Hz
0.5568 RMS VA/lb

@Magnetic Field 1.50 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.3532 RMS AT/cm

@Magnetic Field 1.60 T,
Frequency 50.0 Hz
0.5582 RMS VA/lb

@Magnetic Field 1.60 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.4383 RMS AT/cm

@Magnetic Field 1.60 T,
Frequency 60.0 Hz
0.6927 RMS VA/lb

@Magnetic Field 1.60 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.4774 RMS AT/cm

@Magnetic Field 1.70 T,
Frequency 50.0 Hz
0.7545 RMS VA/lb

@Magnetic Field 1.70 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.5867 RMS AT/cm

@Magnetic Field 1.70 T,
Frequency 60.0 Hz
0.9273 RMS VA/lb

@Magnetic Field 1.70 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.82536 RMS AT/cm

@Magnetic Field 1.80 T,
Frequency 50.0 Hz
1.3045 RMS VA/lb

@Magnetic Field 1.80 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
1.0008 RMS AT/cm

@Magnetic Field 1.80 T,
Frequency 60.0 Hz
1.5818 RMS VA/lb

@Magnetic Field 1.80 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
2.8558 RMS AT/cm

@Magnetic Field 1.90 T,
Frequency 50.0 Hz
4.5136 RMS VA/lb

@Magnetic Field 1.90 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
3.5057 RMS AT/cm

@Magnetic Field 1.90 T,
Frequency 60.0 Hz
5.5409 RMS VA/lb

@Magnetic Field 1.90 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
Electrical Resistivity 0.0000500 ohm-cm
0.0000500 ohm-cm
Magnetic Properties Metric English Comments
Core Loss 0.00289 W/kg

@Magnetic Field 0.100 T,
Frequency 50.0 Hz
0.00131 W/lb

@Magnetic Field 0.100 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.00385 W/kg

@Magnetic Field 0.100 T,
Frequency 60.0 Hz
0.00175 W/lb

@Magnetic Field 0.100 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.01082 W/kg

@Magnetic Field 0.200 T,
Frequency 50.0 Hz
0.004908 W/lb

@Magnetic Field 0.200 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.01451 W/kg

@Magnetic Field 0.200 T,
Frequency 60.0 Hz
0.006582 W/lb

@Magnetic Field 0.200 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0236 W/kg

@Magnetic Field 0.300 T,
Frequency 50.0 Hz
0.0107 W/lb

@Magnetic Field 0.300 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0317 W/kg

@Magnetic Field 0.300 T,
Frequency 60.0 Hz
0.0144 W/lb

@Magnetic Field 0.300 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0413 W/kg

@Magnetic Field 0.400 T,
Frequency 50.0 Hz
0.0187 W/lb

@Magnetic Field 0.400 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0554 W/kg

@Magnetic Field 0.400 T,
Frequency 60.0 Hz
0.0251 W/lb

@Magnetic Field 0.400 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0635 W/kg

@Magnetic Field 0.500 T,
Frequency 50.0 Hz
0.0288 W/lb

@Magnetic Field 0.500 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm
0.0852 W/kg

@Magnetic Field 0.500 T,
Frequency 60.0 Hz
0.0386 W/lb

@Magnetic Field 0.500 T,
Frequency 60.0 Hz
ASTM A804, 0.23 mm
0.0903 W/kg

@Magnetic Field 0.600 T,
Frequency 50.0 Hz
0.0410 W/lb

@Magnetic Field 0.600 T,
Frequency 50.0 Hz
ASTM A804, 0.23 mm